Celanese Celanex® 4202 PBT, 15% Glass Reinforced  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
Manufacturer
Trade Name Celanex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Celanex® 4202 PBT, 15% Glass Reinforced  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Celanex 4202 is a 15% glass reinforced, impact modified polybutylene terephthalate with excellent surface appearance.15% glass-fiber, improved impactInformation provided by Celanese
Physical Properties Metric English Comments
Specific Gravity 1.38 g/cc
1.38 g/cc
ASTM D792
Density 1.38 g/cc
0.0499 lb/in³
ISO 1183
Moisture Absorption 0.160 %
0.160 %
23°C/50%RH; ISO 62
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
ISO 294-4
0.0050 - 0.010 cm/cm
0.0050 - 0.010 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
0.0090 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 84.1 MPa
12200 psi
ASTM D638
86.0 MPa
12500 psi
5mm/min; ISO 527-2/1A
Tensile Strength, Yield 85.5 MPa
12400 psi
ASTM D638
Elongation at Break 4.4 %
4.4 %
5mm/min; ISO 527-2/1A
3.8 %

@Temperature 22.8 °C
3.8 %

@Temperature 73.0 °F
ASTM D638
Tensile Modulus 5.20 GPa
754 ksi
1mm/min; ISO 527-2/1A
4.83 GPa

@Temperature 22.8 °C
700 ksi

@Temperature 73.0 °F
ASTM D638
Flexural Strength 141 MPa
20400 psi
ASTM D790
141 MPa
20500 psi
ISO 178
Flexural Modulus 5.10 GPa
740 ksi
ISO 178
4.41 GPa

@Temperature 22.8 °C
640 ksi

@Temperature 73.0 °F
ASTM D790
Izod Impact, Notched 0.961 J/cm
1.80 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 11.7 kJ/m²
5.57 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched 5.20 J/cm²
24.7 ft-lb/in²
ISO 179/1eU
3.70 J/cm²

@Temperature -30.0 °C
17.6 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 1.07 J/cm²
5.09 ft-lb/in²
ISO 179/1eA
0.570 J/cm²

@Temperature -30.0 °C
2.71 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 36.0 µm/m-°C
20.0 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 100 µm/m-°C
55.6 µin/in-°F
ISO 11359-2
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1,-2,-3
225 °C
437 °F
ASTM D3418
Transformation Temperature, Tg 44.0 °C
111 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 0.46 MPa (66 psi) 216 °C
420 °F
ASTM D648
216 °C
421 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 183 °C
361 °F
ISO 75-1, -2
193 °C
380 °F
ASTM D648
Flammability, UL94 HB
HB
UL94
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+16 ohm-cm
2.00e+16 ohm-cm
IEC 60093
Surface Resistance 1.00e+17 ohm
1.00e+17 ohm
IEC 60093
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz
3.2

@Frequency 1.00e+6 Hz
IEC 60250
3.4

@Frequency 100 Hz
3.4

@Frequency 100 Hz
IEC 60250
Dielectric Strength 22.0 kV/mm
559 kV/in
IEC 60243-1
Dissipation Factor 0.020

@Frequency 1.00e+6 Hz
0.020

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index >= 600 V
>= 600 V
IEC 60112
Processing Properties Metric English Comments
Processing Temperature 20.0 - 50.0 °C
68.0 - 122 °F
65.0 - 93.0 °C
149 - 199 °F
Cavity temperature
Feed Temperature 230 - 240 °C
446 - 464 °F
Rear Barrel Temperature 230 - 240 °C
446 - 464 °F
Middle Barrel Temperature 235 - 250 °C
455 - 482 °F
Front Barrel Temperature 240 - 260 °C
464 - 500 °F
Nozzle Temperature 250 - 260 °C
482 - 500 °F
Zone 1 230 - 240 °C
446 - 464 °F
Zone 2 235 - 250 °C
455 - 482 °F
Zone 3 235 - 250 °C
455 - 482 °F
Zone 4 240 - 260 °C
464 - 500 °F
Die Temperature 250 - 260 °C
482 - 500 °F
Melt Temperature 235 - 260 °C
455 - 500 °F
260 °C
500 °F
Injection molding; ISO 294
Mold Temperature 65.6 - 93.3 °C
150 - 200 °F
82.0 °C
180 °F
Injection molding; ISO 294
Injection Velocity 300 mm/sec
11.8 in/sec
ISO 294
Drying Temperature 120 - 130 °C
248 - 266 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content 0.020 %
0.020 %
Necessary low maximum residual
Hold Pressure 48.0 MPa
6960 psi
ISO 294
Back Pressure 0.000 - 0.345 MPa
0.000 - 50.0 psi
Hot-Working Temperature 250 - 260 °C
482 - 500 °F
Descriptive Properties Value Comments
Injection molding Yes
Injection Speed medium-fast
Longer pre-drying times/storage lower the temperature to 100° C until processed.
<= 60 h
Processing conditions ISO 7792-2
Processing Notes Fast Injection Speed
Medium Screw Speed