Celanese Celanex® 3310 Polyester (PBT), 30% Glass-Fiber

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant
Manufacturer Celanese Corporation
Trade Name Celanex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Celanex® 3310 Polyester (PBT), 30% Glass-Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Flame retardantInformation provided by Celanese Corporation.
Physical Properties Metric English Comments
Density 1.66 g/cc
0.0600 lb/in³
ASTM D792
Water Absorption 0.070 %
0.070 %
ASTM D570
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
Mechanical Properties Metric English Comments
Hardness, Rockwell M 90
90
ISO 2039-2
Tensile Strength, Ultimate 140 MPa
20300 psi
ISO 527
Elongation at Break 2.0 %
2.0 %
ASTM D638
Flexural Strength 225 MPa
32600 psi
ISO 178
Flexural Modulus 10.6 GPa
1540 ksi
ISO 178
Izod Impact, Notched (ISO) 8.40 kJ/m²
4.00 ft-lb/in²
ISO 180/1A
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 222 °C
432 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
ISO 75
Flammability, UL94 V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
UL94
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
ASTM D257
Dielectric Constant 3.9

@Frequency 100 Hz
3.9

@Frequency 100 Hz
Dielectric Strength 19.0 kV/mm

@Thickness 3.17 mm
483 kV/in

@Thickness 0.125 in
50% RH; ASTM D149
Dissipation Factor 0.0060

@Frequency 100 Hz
0.0060

@Frequency 100 Hz
Comparative Tracking Index 280 V
280 V
ASTM D3638