Celanese Celanex® 3300-2LM PBT, Glass Reinforced  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Filled, Impact Modified
Manufacturer
Trade Name Celanex®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Celanex® 3300-2LM PBT, Glass Reinforced  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Celanex 3300-2LM is a 30% glass-filled PBT that is enhanced for improved laser marking graphics. It contains an internal lubricant for enhanced mold release.30% glass-filled PBT, laser markableInformation provided by Celanese
Physical Properties Metric English Comments
Density 1.53 g/cc
0.0553 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm
0.0030 - 0.0050 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Hardness, Rockwell M 90
90
ISO 2039-2
Tensile Strength at Break 130 MPa
18900 psi
5mm/min; ISO 527-2/1A
134 MPa
19500 psi
ASTM D638
Elongation at Break 2.0 %

@Temperature 22.8 °C
2.0 %

@Temperature 73.0 °F
ASTM D638
Flexural Strength 193 MPa
28000 psi
ASTM D790
210 MPa
30500 psi
ISO 178
Flexural Modulus 9.70 GPa
1410 ksi
ISO 178
8.27 GPa

@Temperature 22.8 °C
1200 ksi

@Temperature 73.0 °F
ASTM D790
Izod Impact, Notched 0.908 J/cm
1.70 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 7.50 kJ/m²
3.57 ft-lb/in²
ISO 180/1A
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 228 °C
442 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 206 °C
403 °F
ASTM D648
Flammability, UL94 HB
HB
UL94
Processing Properties Metric English Comments
Processing Temperature 20.0 - 50.0 °C
68.0 - 122 °F
65.0 - 93.0 °C
149 - 199 °F
Cavity temperature
Feed Temperature 230 - 240 °C
446 - 464 °F
Rear Barrel Temperature 230 - 240 °C
446 - 464 °F
Middle Barrel Temperature 235 - 250 °C
455 - 482 °F
Front Barrel Temperature 240 - 260 °C
464 - 500 °F
Nozzle Temperature 250 - 260 °C
482 - 500 °F
Zone 1 230 - 240 °C
446 - 464 °F
Zone 2 235 - 250 °C
455 - 482 °F
Zone 3 235 - 250 °C
455 - 482 °F
Zone 4 240 - 260 °C
464 - 500 °F
Die Temperature 250 - 260 °C
482 - 500 °F
Melt Temperature 235 - 260 °C
455 - 500 °F
Mold Temperature 65.6 - 93.3 °C
150 - 200 °F
Back Pressure 0.000 - 0.345 MPa
0.000 - 50.0 psi
Hot-Working Temperature 250 - 260 °C
482 - 500 °F
Descriptive Properties Value Comments
Processing Notes Fast Injection Speed
Medium Screw Speed