Celanese Celanex® 2002UV PBT, Unfilled

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer Celanese Corporation
Trade Name Celanex®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Celanex® 2002UV PBT, Unfilled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Celanex 2002UV is a general purpose,unreinforced polybutylene terephthalate with a good balance of mechanical properties, processability and UV resistance. Celanex 2002UV is a medium flow materialTo avoid hydrolytic degradation during processing, CELANEX resins have to be dried to a moisture level equal to or less than 0.02%. Drying should be done in a dehumidifying hopper dryer capable of dewpoints
Physical Properties Metric English Comments
Specific Gravity 1.31 g/cc
1.31 g/cc
ASTM D792
Density 1.31 g/cc
0.0473 lb/in³
ISO 1183
Water Absorption 0.090 %

@Temperature 22.8 °C
0.090 %

@Temperature 73.0 °F
24hr immersion; ASTM D570
Linear Mold Shrinkage, Flow 0.018 - 0.020 cm/cm
0.018 - 0.020 in/in
ASTM D955
0.018 - 0.020 cm/cm
0.018 - 0.020 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 57.9 MPa

@Temperature 22.8 °C
8400 psi

@Temperature 73.0 °F
ASTM D638
Tensile Stress 30.0 MPa

@Strain 50.0 %
4350 psi

@Strain 50.0 %
50mm/min; ISO 527-2/1A
Tensile Strength, Yield 60.0 MPa
8700 psi
50mm/min; ISO 527-2/1A
Elongation at Break >= 50 %
>= 50 %
ISO 527-2/1A
45 %

@Temperature 22.8 °C
45 %

@Temperature 73.0 °F
ASTM D638
Elongation at Yield 4.0 %
4.0 %
50mm/min; ISO 527-2/1A
Tensile Modulus 2.60 GPa
377 ksi
1mm/min; ISO 527-2/1A
Flexural Strength 80.0 MPa
11600 psi
ISO 178
86.9 MPa

@Temperature 22.8 °C
12600 psi

@Temperature 73.0 °F
ASTM D790
Flexural Modulus 2.50 GPa
363 ksi
ISO 178
2.74 GPa

@Temperature 22.8 °C
397 ksi

@Temperature 73.0 °F
ASTM D790
Izod Impact, Notched 0.481 J/cm

@Temperature 22.8 °C
0.900 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched NB
NB
ISO 179/1eU
19.0 J/cm²

@Temperature 30.0 °C
90.4 ft-lb/in²

@Temperature 86.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
ISO 179/1eA
0.600 J/cm²

@Temperature 30.0 °C
2.86 ft-lb/in²

@Temperature 86.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 110 µm/m-°C
61.1 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 120 µm/m-°C
66.7 µin/in-°F
ISO 11359-2
Melting Point 225 °C
437 °F
ISO 11357-1,-2,-3
225 °C
437 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 150 °C
302 °F
ISO 75-1, -2
160 °C
320 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
ISO 75-1, -2
55.0 °C
131 °F
ASTM D648
Vicat Softening Point 190 °C
374 °F
B50 (50°C/h 50N); ISO 306
Glass Transition Temp, Tg 60.0 °C
140 °F
ISO 11357-1,-2,-3
Flammability, UL94 HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
IEC 60093
Dielectric Constant 3.5

@Frequency 1.00e+6 Hz
3.5

@Frequency 1.00e+6 Hz
IEC 60250
4.0

@Frequency 100 Hz
4.0

@Frequency 100 Hz
IEC 60250
Dielectric Strength 23.0 kV/mm
584 kV/in
IEC 60243-1
Dissipation Factor 0.0014

@Frequency 100 Hz
0.0014

@Frequency 100 Hz
IEC 60250
0.022

@Frequency 1.00e+6 Hz
0.022

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Processing Temperature 20.0 - 50.0 °C
68.0 - 122 °F
hopper
65.0 - 93.0 °C
149 - 199 °F
cavity
Feed Temperature 230 - 240 °C
446 - 464 °F
Zone 1 230 - 240 °C
446 - 464 °F
Zone 2 235 - 250 °C
455 - 482 °F
Zone 3 235 - 250 °C
455 - 482 °F
Zone 4 240 - 260 °C
464 - 500 °F
Die Temperature 250 - 260 °C
482 - 500 °F
Melt Temperature 235 - 260 °C
455 - 500 °F
Drying Temperature 120 - 130 °C
248 - 266 °F
Dry Time 4 hour
4 hour
Moisture Content 0.020 %
0.020 %
Necessary low maximum
Hot-Working Temperature 250 - 260 °C
482 - 500 °F