Celanese Celanex® 2002AP Unreinforced Polybutylene Terephthalate

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Unreinforced, Molded
Manufacturer Celanese Corporation
Trade Name Celanex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Celanex® 2002AP Unreinforced Polybutylene Terephthalate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Celanex 2002AP is a general purpose, unreinforced polybutylene terephthalate with a good balance of mechanical properties, processability and UV and heat resistance. Celanex 2002AP is a medium flow material. It was designed for home appliance parts.Information provided by Celanese Corporation.
Physical Properties Metric English Comments
Density 1.31 g/cc
0.0473 lb/in³
ISO 1183
Mechanical Properties Metric English Comments
Tensile Strength, Yield 60.0 MPa
8700 psi
50 mm/min; ISO 527-2/1A
Elongation at Break >= 50 %
>= 50 %
50 mm/min; ISO 527-2/1A
Elongation at Yield 4.0 %
4.0 %
50 mm/min; ISO 527-2/1A
Tensile Modulus 2.60 GPa
377 ksi
1 mm/min; ISO 527-2/1A
Flexural Strength 80.0 MPa
11600 psi
ISO 178
Flexural Modulus 2.50 GPa
363 ksi
ISO 178
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched NB
NB
ISO 179/1eU
19.0 J/cm²

@Temperature -30.0 °C
90.4 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
ISO 179/1eA
0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Thermal Properties Metric English Comments
CTE, linear 110 µm/m-°C

@Temperature 20.0 °C
61.1 µin/in-°F

@Temperature 68.0 °F
ISO 11359-2
Melting Point 225 °C
437 °F
ISO 11357-1,2,3
Deflection Temperature at 0.46 MPa (66 psi) 150 °C
302 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
ISO 75-1, -2
Flammability, UL94 HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
IEC 60093
Dielectric Constant 3.5

@Frequency 1e+6 Hz
3.5

@Frequency 1e+6 Hz
IEC 60250
4.0

@Frequency 100 Hz
4.0

@Frequency 100 Hz
IEC 60250
Dielectric Strength 23.0 kV/mm
584 kV/in
IEC 60243-1
Dissipation Factor 0.0014

@Frequency 100 Hz
0.0014

@Frequency 100 Hz
IEC 60250
0.022

@Frequency 1e+6 Hz
0.022

@Frequency 1e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Rear Barrel Temperature 230 - 240 °C
446 - 464 °F
Middle Barrel Temperature 235 - 250 °C
455 - 482 °F
Front Barrel Temperature 240 - 260 °C
464 - 500 °F
Nozzle Temperature 250 - 260 °C
482 - 500 °F
Melt Temperature 235 - 260 °C
455 - 500 °F
Mold Temperature 65.0 - 93.0 °C
149 - 199 °F
Drying Temperature 121 °C
250 °F
Dry Time 4 hour
4 hour
Back Pressure 0.000 - 0.345 MPa
0.000 - 50.0 psi