Celanese CELANEX 5202 PBT, 15% Glass Reinforced

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
Manufacturer Celanese Corporation
Trade Name CELANEX
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese CELANEX 5202 PBT, 15% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Celanex 5202 is a 15% glass filled polyester that features improved surface gloss and has an excellent balance of mechanical properties, processability, and color stability under heat and UV exposure. A typical application for Celanex 5202 is oven handles.Information provided by Celanese
Physical Properties Metric English Comments
Density 1.44 g/cc
0.0520 lb/in³
ISO 1183
Moisture Absorption 0.170 %
0.170 %
23°C/50%RH; ISO 62
Linear Mold Shrinkage, Flow 0.00100 - 0.00600 cm/cm
0.00100 - 0.00600 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.00700 cm/cm
0.00700 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa
14500 psi
5mm/min; ISO 527-2/1A
Elongation at Break 2.50 %
2.50 %
5mm/min; ISO 527-2/1A
Tensile Modulus 6.10 GPa
885 ksi
50mm/min; ISO 527-2/1A
Flexural Strength 150 MPa
21800 psi
ISO 178
Flexural Modulus 5.30 GPa
769 ksi
ISO 178
Izod Impact, Notched (ISO) 4.40 kJ/m²
2.09 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched 1.50 J/cm²
7.14 ft-lb/in²
ISO 179/1eU
1.70 J/cm²

@Temperature -30.0 °C
8.09 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.470 J/cm²
2.24 ft-lb/in²
ISO 179/1eA
0.450 J/cm²

@Temperature -30.0 °C
2.14 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 42.0 µm/m-°C
23.3 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 73.0 µm/m-°C
40.6 µin/in-°F
ISO 11359-2
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 180 °C
356 °F
ISO 75-1, -2
Glass Transition Temp, Tg 50.0 °C
122 °F
ISO 11357-1,-2,-3
Flammability, UL94 HB
HB
HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
Electrical Properties Metric English Comments
Volume Resistivity 7.00e+16 ohm-cm
7.00e+16 ohm-cm
IEC 60093
Surface Resistance 4.00e+15 ohm
4.00e+15 ohm
IEC 60093
Dielectric Constant 2.70

@Frequency 100 Hz
2.70

@Frequency 100 Hz
IEC 60250
2.70

@Frequency 1.00e+6 Hz
2.70

@Frequency 1.00e+6 Hz
IEC 60250
Dielectric Strength 17.0 kV/mm
432 kV/in
IEC 60243-1
Dissipation Factor 0.0140

@Frequency 1.00e+6 Hz
0.0140

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 225 V
225 V
IEC 60112
Processing Properties Metric English Comments
Processing Temperature 65.0 - 93.0 °C
149 - 199 °F
cavity
250 - 265 °C
482 - 509 °F
hot runner
Feed Temperature 230 - 250 °C
446 - 482 °F
Middle Barrel Temperature 20.0 - 50.0 °C
68.0 - 122 °F
Zone 1 230 - 250 °C
446 - 482 °F
Zone 2 235 - 255 °C
455 - 491 °F
Zone 3 235 - 255 °C
455 - 491 °F
Zone 4 240 - 260 °C
464 - 500 °F
Die Temperature 250 - 265 °C
482 - 509 °F
Melt Temperature 235 - 265 °C
455 - 509 °F
Drying Temperature 120 - 130 °C
248 - 266 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content <= 0.0200 %
<= 0.0200 %
Descriptive Properties Value Comments
Injection molding Yes
Injection Speed medium-fast