Celanese CELANEX 5200-2 PBT, 15% Glass Reinforced

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
Manufacturer Celanese Corporation
Trade Name CELANEX
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese CELANEX 5200-2 PBT, 15% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Celanex 5200-2 is a 15% fiberglass reinforced polyester with improved surface finish. Celanex 5200-2 contains an internal lubricant.Information provided by Celanese
Physical Properties Metric English Comments
Specific Gravity 1.41 g/cc
1.41 g/cc
ASTM D792
Density 1.41 g/cc
0.0509 lb/in³
ISO 1183
Water Absorption 0.0500 %

@Temperature 22.8 °C
0.0500 %

@Temperature 73.0 °F
24hr immersion; ASTM D570
Moisture Absorption 0.200 %
0.200 %
23°C/50%RH; ISO 62
Viscosity Test 69.0 cm³/g
69.0 cm³/g
ISO 307, 1157, 1628
Linear Mold Shrinkage, Flow 0.00400 - 0.00600 cm/cm
0.00400 - 0.00600 in/in
ISO 294-4
0.00400 - 0.00600 cm/cm
0.00400 - 0.00600 in/in
ASTM D955
Melt Flow 28.0 g/10 min
28.0 g/10 min
ASTM D1238
38.0 g/10 min

@Load 2.16 kg,
Temperature 265 °C
38.0 g/10 min

@Load 4.76 lb,
Temperature 509 °F
[cm3/10min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 91.0
91.0
ISO 2039-2
Tensile Strength at Break 89.6 MPa
13000 psi
ASTM D638
120 MPa
17400 psi
5mm/min; ISO 527-2/1A
Elongation at Break 2.00 %
2.00 %
ASTM D638
3.00 %
3.00 %
5mm/min; ISO 527-2/1A
Tensile Modulus 6.00 GPa
870 ksi
50mm/min; ISO 527-2/1A
Flexural Strength 152 MPa
22000 psi
ASTM D790
185 MPa
26800 psi
ISO 178
Flexural Modulus 6.07 GPa
880 ksi
ASTM D790
8.00 GPa
1160 ksi
ISO 178
Izod Impact, Notched 0.534 J/cm
1.00 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 7.10 kJ/m²
3.38 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched 3.50 J/cm²
16.7 ft-lb/in²
ISO 179/1eU
3.50 J/cm²

@Temperature -30.0 °C
16.7 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
ISO 179/1eA
0.800 J/cm²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 35.0 µm/m-°C
19.4 µin/in-°F
ISO 11359-2
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1,-2,-3
225 °C
437 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ISO 75-1, -2
216 °C
420 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 179 °C
355 °F
ASTM D648
190 °C
374 °F
ISO 75-1, -2
Deflection Temperature at 8.0 MPa 65.0 °C
149 °F
ISO 75-1, -2
Vicat Softening Point 210 °C
410 °F
ISO 306
Flammability, UL94 HB
HB
HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
Oxygen Index 20.0 %
20.0 %
ISO 4589
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.70

@Frequency 1.00e+6 Hz
3.70

@Frequency 1.00e+6 Hz
ASTM D150
4.00

@Frequency 1.00e+6 Hz
4.00

@Frequency 1.00e+6 Hz
IEC 60250
4.30

@Frequency 100 Hz
4.30

@Frequency 100 Hz
IEC 60250
Dielectric Strength 19.3 kV/mm
490 kV/in
short term; ASTM D149
28.0 kV/mm
711 kV/in
IEC 60243-1
Dissipation Factor 0.00110

@Frequency 100 Hz
0.00110

@Frequency 100 Hz
IEC 60250
0.00200

@Frequency 1.00e+6 Hz
0.00200

@Frequency 1.00e+6 Hz
ASTM D150
0.0190

@Frequency 1.00e+6 Hz
0.0190

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 325 V
325 V
IEC 60112
Processing Properties Metric English Comments
Processing Temperature 65.0 - 93.0 °C
149 - 199 °F
cavity
250 - 265 °C
482 - 509 °F
hot runner
Feed Temperature 230 - 250 °C
446 - 482 °F
Middle Barrel Temperature 20.0 - 50.0 °C
68.0 - 122 °F
Zone 1 230 - 250 °C
446 - 482 °F
Zone 2 235 - 255 °C
455 - 491 °F
Zone 3 235 - 255 °C
455 - 491 °F
Zone 4 240 - 260 °C
464 - 500 °F
Die Temperature 250 - 265 °C
482 - 509 °F
Melt Temperature 235 - 265 °C
455 - 509 °F
260 °C
500 °F
ISO 294
Mold Temperature 82.0 °C
180 °F
ISO 294
Injection Velocity 300 mm/sec
11.8 in/sec
ISO 294
Drying Temperature 120 - 130 °C
248 - 266 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content <= 0.0200 %
<= 0.0200 %
Hold Pressure 48.0 MPa
6960 psi
ISO 294
Descriptive Properties Value Comments
Injection molding Yes
Injection Speed medium-fast
Processing conditions acc. ISO 7792-2