Celanese CELANEX 3309HRLM PBT, 30% Glass Reinforced

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer Celanese Corporation
Trade Name CELANEX
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese CELANEX 3309HRLM PBT, 30% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Celanex 3309HRLM is a non-lubricated, 30% fiberglass reinforced Polybutylene Terephthalate which has excellent hydrolysis resistance, mechanical properties and processability. lIt is a asermarkable grade available in a black color to mark white The grade is specially formulated to yield crisp marks when subjected to a Nd:YAG laser or equivalent operated at 1064nm or 532nm. Lasers operating in the UV region (355nm) may yield different resultsInformation provided by Celanese
Physical Properties Metric English Comments
Specific Gravity 1.53 g/cc
1.53 g/cc
ASTM D792
Density 1.55 g/cc
0.0560 lb/in³
ISO 1183
Moisture Absorption 0.150 %
0.150 %
23°C/50%RH; ISO 62
Linear Mold Shrinkage, Flow 0.00300 - 0.00500 cm/cm
0.00300 - 0.00500 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.00700 - 0.00900 cm/cm
0.00700 - 0.00900 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 135 MPa
19600 psi
5mm/min; ISO 527-2/1A
136.2 MPa
19750 psi
ASTM D638
Elongation at Break 2.70 %
2.70 %
5mm/min; ISO 527-2/1A
2.80 %
2.80 %
ASTM D638
Tensile Modulus 9.20 GPa
1330 ksi
50mm/min; ISO 527-2/1A
Flexural Strength 210 MPa
30500 psi
ISO 178
211.3 MPa
30650 psi
ASTM D790
Flexural Modulus 8.48 GPa
1230 ksi
ASTM D790
8.90 GPa
1290 ksi
ISO 178
Izod Impact, Notched 1.07 J/cm
2.00 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
ISO 180/1A
35.0 kJ/m²

@Temperature 23.0 °C
16.7 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched 4.60 J/cm²
21.9 ft-lb/in²
ISO 179/1eU
4.50 J/cm²

@Temperature -30.0 °C
21.4 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.650 J/cm²
3.09 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.0 µm/m-°C
13.9 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 100 µm/m-°C
55.6 µin/in-°F
ISO 11359-2
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 0.46 MPa (66 psi) 225 °C
437 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 208 °C
406 °F
ISO 75-1, -2
Vicat Softening Point 220 °C
428 °F
ISO 306
Glass Transition Temp, Tg 60.0 °C
140 °F
ISO 11357-1,-2,-3
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 4.10

@Frequency 1.00e+6 Hz
4.10

@Frequency 1.00e+6 Hz
IEC 60250
4.50

@Frequency 100 Hz
4.50

@Frequency 100 Hz
IEC 60250
Dielectric Strength 31.0 kV/mm
787 kV/in
IEC 60243-1
Dissipation Factor 0.00220

@Frequency 100 Hz
0.00220

@Frequency 100 Hz
IEC 60250
0.0160

@Frequency 1.00e+6 Hz
0.0160

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 425 V
425 V
IEC 60112
Processing Properties Metric English Comments
Processing Temperature 65.0 - 93.0 °C
149 - 199 °F
cavity
250 - 260 °C
482 - 500 °F
hot runner
Feed Temperature 230 - 240 °C
446 - 464 °F
Middle Barrel Temperature 20.0 - 50.0 °C
68.0 - 122 °F
Zone 1 230 - 240 °C
446 - 464 °F
Zone 2 235 - 250 °C
455 - 482 °F
Zone 3 235 - 250 °C
455 - 482 °F
Zone 4 240 - 260 °C
464 - 500 °F
Die Temperature 250 - 260 °C
482 - 500 °F
Melt Temperature 235 - 260 °C
455 - 500 °F
Drying Temperature 120 - 130 °C
248 - 266 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content <= 0.0200 %
<= 0.0200 %
Descriptive Properties Value Comments
Injection molding Yes