Celanese CELANEX 3300-2 PBT, 30% Glass Reinforced

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer Celanese Corporation
Trade Name CELANEX
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese CELANEX 3300-2 PBT, 30% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Celanex 3300-2 is a general purpose, 30% glass reinforced, polybutylene terephthalate that offers a superior combination of mechanical, electrical, and thermal properties. This grade provides outstanding processability and good chemical resistance. Celanex 3300-2 is a high flow material that contains an internal lubricant.Information provided by Celanese
Physical Properties Metric English Comments
Specific Gravity 1.53 g/cc
1.53 g/cc
ASTM D792
Density 1.53 g/cc
0.0553 lb/in³
ISO 1183
Water Absorption 0.0700 %

@Temperature 22.8 °C
0.0700 %

@Temperature 73.0 °F
24hr immersion; ASTM D570
Moisture Absorption 0.200 %
0.200 %
23°C/50%RH; ISO 62
Viscosity Test 74.0 cm³/g
74.0 cm³/g
ISO 307, 1157, 1628
Linear Mold Shrinkage, Flow 0.00300 - 0.00500 cm/cm
0.00300 - 0.00500 in/in
ASTM D955
0.00300 - 0.00700 cm/cm
0.00300 - 0.00700 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.00700 - 0.0110 cm/cm
0.00700 - 0.0110 in/in
ISO 294-4
Melt Flow 16.0 g/10 min
16.0 g/10 min
ASTM D1238
17.0 g/10 min

@Load 2.16 kg,
Temperature 250 °C
17.0 g/10 min

@Load 4.76 lb,
Temperature 482 °F
[cm3/10min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 90.0
90.0
ISO 2039-2
Tensile Strength at Break 130 MPa
18900 psi
5mm/min; ISO 527-2/1A
134 MPa
19500 psi
ASTM D638
61.4 MPa

@Temperature 121 °C
8900 psi

@Temperature 250 °F
ASTM D638
77.57 MPa

@Temperature 80.0 °C
11250 psi

@Temperature 176 °F
ASTM D638
159 MPa

@Temperature 0.000 °C
23000 psi

@Temperature 32.0 °F
ASTM D638
190 MPa

@Temperature -40.0 °C
27500 psi

@Temperature -40.0 °F
ASTM D638
Elongation at Break 2.00 %
2.00 %
ASTM D638
2.50 %
2.50 %
5mm/min; ISO 527-2/1A
1.90 %

@Temperature 0.000 °C
1.90 %

@Temperature 32.0 °F
ASTM D638
1.90 %

@Temperature 4.44 °C
1.90 %

@Temperature 40.0 °F
ASTM D638
3.90 %

@Temperature 80.0 °C
3.90 %

@Temperature 176 °F
ASTM D638
4.30 %

@Temperature 121 °C
4.30 %

@Temperature 250 °F
ASTM D638
Tensile Modulus 9.20 GPa
1330 ksi
50mm/min; ISO 527-2/1A
9.65 GPa
1400 ksi
ASTM D638
3.76 GPa

@Temperature 121 °C
545 ksi

@Temperature 250 °F
ASTM D638
4.83 GPa

@Temperature 80.0 °C
700 ksi

@Temperature 176 °F
ASTM D638
10.5 GPa

@Temperature 0.000 °C
1520 ksi

@Temperature 32.0 °F
ASTM D638
11.0 GPa

@Temperature -40.0 °C
1600 ksi

@Temperature -40.0 °F
ASTM D638
Flexural Strength 193 MPa
28000 psi
ASTM D790
210 MPa
30500 psi
ISO 178
Flexural Modulus 8.27 GPa
1200 ksi
ASTM D790
9.70 GPa
1410 ksi
ISO 178
Izod Impact, Notched 0.908 J/cm
1.70 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 7.50 kJ/m²
3.57 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched 4.60 J/cm²
21.9 ft-lb/in²
ISO 179/1eU
4.50 J/cm²

@Temperature -30.0 °C
21.4 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.850 J/cm²
4.04 ft-lb/in²
ISO 179/1eA
0.850 J/cm²

@Temperature -30.0 °C
4.04 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.0 µm/m-°C
13.9 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 100 µm/m-°C
55.6 µin/in-°F
ISO 11359-2
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1,-2,-3
225 °C
437 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 225 °C
437 °F
ISO 75-1, -2
228 °C
442 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
ISO 75-1, -2
206 °C
403 °F
ASTM D648
Deflection Temperature at 8.0 MPa 150 °C
302 °F
ISO 75-1, -2
Vicat Softening Point 220 °C
428 °F
ISO 306
Glass Transition Temp, Tg 60.0 °C
140 °F
ISO 11357-1,-2,-3
Flammability, UL94 HB

@Thickness 0.710 mm
HB

@Thickness 0.0280 in
Oxygen Index 20.0 %
20.0 %
ISO 4589
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.70

@Frequency 1.00e+6 Hz
3.70

@Frequency 1.00e+6 Hz
ASTM D150
4.10

@Frequency 1.00e+6 Hz
4.10

@Frequency 1.00e+6 Hz
IEC 60250
4.50

@Frequency 100 Hz
4.50

@Frequency 100 Hz
IEC 60250
Dielectric Strength 22.0 kV/mm
560 kV/in
short term; ASTM D149
31.0 kV/mm
787 kV/in
IEC 60243-1
Dissipation Factor 0.00200

@Frequency 1.00e+6 Hz
0.00200

@Frequency 1.00e+6 Hz
ASTM D150
0.00220

@Frequency 100 Hz
0.00220

@Frequency 100 Hz
IEC 60250
0.0160

@Frequency 1.00e+6 Hz
0.0160

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 425 V
425 V
IEC 60112
Processing Properties Metric English Comments
Processing Temperature 65.0 - 93.0 °C
149 - 199 °F
cavity
250 - 260 °C
482 - 500 °F
hot runner
Feed Temperature 230 - 240 °C
446 - 464 °F
Middle Barrel Temperature 20.0 - 50.0 °C
68.0 - 122 °F
Zone 1 230 - 240 °C
446 - 464 °F
Zone 2 235 - 250 °C
455 - 482 °F