Celanese CELANEX 3216HR PBT, 15% Glass Reinforced

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
Manufacturer Celanese Corporation
Trade Name CELANEX
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese CELANEX 3216HR PBT, 15% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Celanex 3216HR is a flame retarded, hydrolysis resistant, 15% fiberglass reinforced polybutylene terephthalate which has an excellent balance of mechanical properties and processability.Information provided by Celanese
Physical Properties Metric English Comments
Density 1.507 g/cc
0.05444 lb/in³
ISO 1183
Mechanical Properties Metric English Comments
Tensile Strength at Break 80.0 MPa
11600 psi
5mm/min; ISO 527-2/1A
Elongation at Break 4.20 %
4.20 %
5mm/min; ISO 527-2/1A
Tensile Modulus 6.00 GPa
870 ksi
50mm/min; ISO 527-2/1A
Flexural Strength 140 MPa
20300 psi
ISO 178
Flexural Modulus 5.30 GPa
769 ksi
ISO 178
Charpy Impact Unnotched 0.800 J/cm²
3.81 ft-lb/in²
ISO 179/1eU
Thermal Properties Metric English Comments
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 1.8 MPa (264 psi) 152 °C
306 °F
ISO 75-1, -2
Flammability, UL94 V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
Processing Properties Metric English Comments
Processing Temperature 65.0 - 96.0 °C
149 - 205 °F
cavity
250 - 260 °C
482 - 500 °F
hot runner
Feed Temperature 230 - 240 °C
446 - 464 °F
Middle Barrel Temperature 20.0 - 50.0 °C
68.0 - 122 °F
Zone 1 230 - 240 °C
446 - 464 °F
Zone 2 235 - 250 °C
455 - 482 °F
Zone 3 235 - 250 °C
455 - 482 °F
Zone 4 240 - 255 °C
464 - 491 °F
Die Temperature 240 - 255 °C
464 - 491 °F
Melt Temperature 235 - 255 °C
455 - 491 °F
260 °C
500 °F
ISO 294
Mold Temperature 82.0 °C
180 °F
ISO 294
Injection Velocity 300 mm/sec
11.8 in/sec
ISO 294
Drying Temperature 120 - 130 °C
248 - 266 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content <= 0.0200 %
<= 0.0200 %
Hold Pressure 48.0 MPa
6960 psi
ISO 294
Descriptive Properties Value Comments
Injection molding Yes
Injection Speed medium-fast
Processing conditions acc. ISO 7792-2
Copyright © lookpolymers.com All Rights Reserved