Celanese CELANEX 1642Z PBT, 20% Glass Reinforced

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
Manufacturer Celanese Corporation
Trade Name CELANEX
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese CELANEX 1642Z PBT, 20% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Celanex 1642Z is a general purpose, 20% fiberglass reinforced PBT with a good balance of mechanical properties and processability.Information provided by Celanese
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.00400 - 0.00800 cm/cm
0.00400 - 0.00800 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 96.5 MPa
14000 psi
ASTM D638
105 MPa
15200 psi
5mm/min; ISO 527-2/1A
Elongation at Break 4.00 %
4.00 %
5mm/min; ISO 527-2/1A
4.00 %
4.00 %
ASTM D638
Tensile Modulus 6.25 GPa
906 ksi
50mm/min; ISO 527-2/1A
Flexural Strength 170 MPa
24700 psi
ISO 178
172 MPa
25000 psi
ASTM D790
Flexural Modulus 5.50 GPa
798 ksi
ISO 178
5.52 GPa
800 ksi
ASTM D790
Izod Impact, Notched 0.694 J/cm
1.30 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 7.50 kJ/m²
3.57 ft-lb/in²
ISO 180/1A
Charpy Impact, Notched 0.630 J/cm²
3.00 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 31.0 µm/m-°C
17.2 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 120 µm/m-°C
66.7 µin/in-°F
ISO 11359-2
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Arc Resistance 130 sec
130 sec
ASTM D495
Processing Properties Metric English Comments
Processing Temperature 65.0 - 93.0 °C
149 - 199 °F
cavity
250 - 260 °C
482 - 500 °F
hot runner
Feed Temperature 230 - 240 °C
446 - 464 °F
Middle Barrel Temperature 20.0 - 50.0 °C
68.0 - 122 °F
Zone 1 230 - 240 °C
446 - 464 °F
Zone 2 235 - 250 °C
455 - 482 °F
Zone 3 235 - 250 °C
455 - 482 °F
Zone 4 240 - 260 °C
464 - 500 °F
Die Temperature 250 - 260 °C
482 - 500 °F
Melt Temperature 235 - 260 °C
455 - 500 °F