Celanese CELANEX 1462Z PBT, 30% Glass Reinforced

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer Celanese Corporation
Trade Name CELANEX
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese CELANEX 1462Z PBT, 30% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Celanex 1462Z is a general purpose, 30% glass reinforced polybutylene terephthalate with a good balance of mechanical properties and processability.Information provided by Celanese
Physical Properties Metric English Comments
Specific Gravity 1.52 g/cc
1.52 g/cc
ASTM D792
Density 1.52 g/cc
0.0549 lb/in³
ISO 1183
Water Absorption 0.0500 %

@Temperature 22.8 °C
0.0500 %

@Temperature 73.0 °F
24hr immersion; ASTM D570
Linear Mold Shrinkage, Flow 0.00300 - 0.00500 cm/cm
0.00300 - 0.00500 in/in
ISO 294-4
0.00300 - 0.00500 cm/cm
0.00300 - 0.00500 in/in
ASTM D955
Melt Flow 14.0 g/10 min
14.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 90.0
90.0
ISO 2039-2
Tensile Strength at Break 124 MPa
18000 psi
ASTM D638
135 MPa
19600 psi
5mm/min; ISO 527-2/1A
Elongation at Break 2.60 %
2.60 %
5mm/min; ISO 527-2/1A
4.00 %
4.00 %
ASTM D638
Flexural Strength 197 MPa
28500 psi
ASTM D790
210 MPa
30500 psi
ISO 178
Flexural Modulus 8.27 GPa
1200 ksi
ASTM D790
9.11 GPa
1320 ksi
ISO 178
Izod Impact, Notched 0.908 J/cm
1.70 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 9.20 kJ/m²
4.38 ft-lb/in²
ISO 180/1A
Charpy Impact, Notched 0.720 J/cm²
3.43 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.0 µm/m-°C
13.9 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 128 µm/m-°C
71.1 µin/in-°F
ISO 11359-2
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1,-2,-3
225 °C
437 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 217 °C
422 °F
ASTM D648
225 °C
437 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 204 °C
400 °F
ASTM D648
207 °C
405 °F
ISO 75-1, -2
Glass Transition Temp, Tg 60.0 °C
140 °F
ISO 11357-1,-2,-3
Flammability, UL94 HB
HB
HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Dielectric Strength 20.5 kV/mm
520 kV/in
short term; ASTM D149
Dissipation Factor 0.00200

@Frequency 1000 Hz
0.00200

@Frequency 1000 Hz
ASTM D150
Processing Properties Metric English Comments
Processing Temperature 65.0 - 93.0 °C
149 - 199 °F
cavity
250 - 260 °C
482 - 500 °F
hot runner
Feed Temperature 230 - 240 °C
446 - 464 °F
Middle Barrel Temperature 20.0 - 50.0 °C
68.0 - 122 °F
Zone 1 230 - 240 °C
446 - 464 °F
Zone 2 235 - 250 °C
455 - 482 °F
Zone 3 235 - 250 °C
455 - 482 °F
Zone 4 240 - 260 °C
464 - 500 °F
Die Temperature 250 - 260 °C
482 - 500 °F
Melt Temperature 235 - 260 °C
455 - 500 °F
260 °C
500 °F
ISO 294
Mold Temperature 82.0 °C
180 °F
ISO 294
Injection Velocity 300 mm/sec
11.8 in/sec
ISO 294
Drying Temperature 120 - 130 °C
248 - 266 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content <= 0.0200 %
<= 0.0200 %
Hold Pressure 48.0 MPa
6960 psi
ISO 294
Descriptive Properties Value Comments
Injection molding Yes
Injection Speed medium-fast
Processing conditions acc. ISO 7792-2