Celanese Ateva® 1210AT Film Ethylene Vinyl Acetate Copolymer Film  (discontinued **)

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Ateva® 1210AT Film Ethylene Vinyl Acetate Copolymer Film  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ateva® 1210AT resin is suitable for co-extrusion and blending applications where superior strength, good heat seal, and hot tack characteristics are required. This EVA resin may be safely used as articles or components of articles intended for uses in contact with food as provided in FDA regulation 21 CFR 177.1350 - Ethylene-vinyl acetate copolymers, subject to extraction limitations on the finished food-contact article as specified in that regulation. It is recommended that the melt temperature be kept below 210°C as decomposition can occur at higher temperatures. Properties listed are for a film produced on a 24:1 L/D, 40 mm extruder with a 100 mm die, at a melting temperature of 210°C. Additives: AntioxidantApplications: Flexible PackagingInformation provided by Celanese Corporation.
Physical Properties Metric English Comments
Density 0.932 g/cc
0.0337 lb/in³
ASTM D1505; ASTM D1928 Proc A
Vinyl Acetate Content 12 %
12 %
AT Plastics PTM-39
Thickness 50.0 microns
1.97 mil
Melt Flow 0.40 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.40 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 8.00 MPa
1160 psi
Method A (500 mm/min); ASTM D882
Film Tensile Strength at Yield, TD 6.00 MPa
870 psi
Method A (500 mm/min); ASTM D882
Film Elongation at Break, MD 410 %
410 %
Method A (500 mm/min); ASTM D882
Film Elongation at Break, TD 510 %
510 %
Method A (500 mm/min); ASTM D882
Dart Drop 10.0 g/micron
254 g/mil
f50; ASTM D1709
Film Tensile Strength at Break, MD 29.0 MPa
4210 psi
Method A (500 mm/min); ASTM D882
Film Tensile Strength at Break, TD 31.0 MPa
4500 psi
Method A (500 mm/min); ASTM D882
Thermal Properties Metric English Comments
Melting Point 97.0 °C
207 °F
DSC; ASTM D3417
Vicat Softening Point 78.0 °C
172 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 19 %
19 %
ASTM D1003
Gloss 30 %
30 %
45°; ASTM D2457
Processing Properties Metric English Comments
Blow-up Ratio (BUR) 2.1
2.1