Celanese Ateva® 1075A Ethylene Vinyl Acetate Copolymer

Category Polymer , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate; Molded/Extruded
Manufacturer Celanese Corporation
Trade Name Ateva®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Ateva® 1075A Ethylene Vinyl Acetate Copolymer.pdf
  Online Service   lookpolymers   27660005
Material Notes:
Ateva® 1075A resin is designed for compound and masterbatch applications, it is also suitable for extrusion and injection molding applications. This EVA resin may be safely used as articles or components of articles intended for uses in contact with food as provided in FDA regulation 21 CFR 177.1350 - Ethylene-vinyl acetate copolymers, subject to extraction limitations on the finished food-contact article as specified in that regulation. This polymer may be processed on conventional extrusion equipment. It is recommended that the melt temperature be kept below 210°C as decomposition can occur at higher temperatures. Additives: AntioxidantApplications: Compounds & Masterbatches; Molding & MiscellaneousInformation provided by Celanese Corporation.
Physical Properties Metric English Comments
Density 0.924 g/cc
0.0334 lb/in³
ASTM D1505; ASTM D1928 Proc A
Vinyl Acetate Content 9.0 %
9.0 %
AT Plastics PTM-39
Melt Flow 8.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
8.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 94
ASTM D2240
Hardness, Shore D 46
ASTM D2240
Tensile Strength at Break 15.0 MPa
2180 psi
Type IV (50 mm/min); ASTM D638
Elongation at Break 692 %
692 %
Type IV (50 mm/min); ASTM D638
Flexural Modulus 0.115 GPa
16.7 ksi
1% Secant; ASTM D790
Thermal Properties Metric English Comments
Melting Point 98.0 °C
208 °F
Vicat Softening Point 79.0 °C
174 °F
ASTM D1525
Brittleness Temperature <= -70.0 °C
<= -94.0 °F