Celanese Ateva® 1062ASB Ethylene Vinyl Acetate Copolymer Film  (discontinued **)

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Ateva® 1062ASB Ethylene Vinyl Acetate Copolymer Film  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ateva® 1062ASB resin is suitable for co-extrusion applications with excellent sealability, strength, and low COF. This EVA resin may be safely used as articles or components of articles intended for uses in contact with food as provided in FDA regulation 21 CFR 177.1350 - Ethylene-vinyl acetate copolymers, subject to extraction limitations on the finished food-contact article as specified in that regulation. Properties listed are for a film produced on a three layer co-extrusion with a 76 mm die, at a stock temperature of 210°C. Additives: Slip / AntiblockApplications: Flexible PackagingInformation provided by Celanese Corporation.
Physical Properties Metric English Comments
Density 0.927 g/cc
0.0335 lb/in³
ASTM D1505; ASTM D1928 Proc A
Vinyl Acetate Content 6.0 %
6.0 %
AT Plastics PTM-39
Thickness 60.0 microns
2.36 mil
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 9.00 MPa
1310 psi
Method A (500 mm/min); ASTM D882
Film Tensile Strength at Yield, TD 10.0 MPa
1450 psi
Method A (500 mm/min); ASTM D882
Film Elongation at Break, MD 360 %
360 %
Method A (500 mm/min); ASTM D882
Film Elongation at Break, TD 500 %
500 %
Method A (500 mm/min); ASTM D882
Secant Modulus, MD 0.120 GPa
17.4 ksi
1% Secant Modulus; ASTM D882
Secant Modulus, TD 0.130 GPa
18.9 ksi
1% Secant Modulus; ASTM D882
Dart Drop 2.80 g/micron
71.1 g/mil
f50; ASTM D1709
Film Tensile Strength at Break, MD 22.0 MPa
3190 psi
Method A (500 mm/min); ASTM D882
Film Tensile Strength at Break, TD 19.0 MPa
2760 psi
Method A (500 mm/min); ASTM D882
Thermal Properties Metric English Comments
Melting Point 103 °C
217 °F
DSC; ASTM D3417
Optical Properties Metric English Comments
Haze 15 %
15 %
ASTM D1003
Gloss 45 %
45 %
45°; ASTM D2457
Processing Properties Metric English Comments
Blow-up Ratio (BUR) 2.0