Carpenter No. 883® Hot Work Die Steel (Red-Tough) (AISI H13)

Category Metal , Ferrous Metal , Tool Steel , Hot Work Steel
Manufacturer Carpenter Technology Corporation (Cartech)
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Carpenter No. 883® Hot Work Die Steel (Red-Tough) (AISI H13).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
No. 883 hot work die steel is a 5% chromium hot work tool steel designed particularly for applications requiring extreme toughness combined with good red-hardness. It has given an extra margin of safety in tools subject to heavy hammer blows, and those tools containing deep recesses or sharp corners. While No. 833 hot work die steel has been used primarily in hot work tools, it has solved many cold work applications where extra toughness was required at the sacrifice of some wear resistance.Applications: Forging dies, Heavy duty compression tools, Bulldozer dies, Hot forging tools with deep recesses and sharp corners, Die casting dies, Aluminum extrusion dies, Bolt dies, Hot piercing punches, Forming punches, Vastoning diesInformation provided by Carpenter Technology Corporation.No. 883® is a registered trademark of Carpenter Technology Corporation.
Physical Properties Metric English Comments
Specific Gravity 7.77 g/cc
7.77 g/cc
Mechanical Properties Metric English Comments
Hardness, Brinell 360

@Temperature 538 °C
360

@Temperature 1000 °F
495

@Temperature 204 °C
495

@Temperature 400 °F
Hardness, Rockwell C 28 - 30
28 - 30
Tempered at 1300°F
51 - 53
51 - 53
As hardened
Tensile Strength, Ultimate 1800 MPa
261000 psi
when tempered at 1000°F
Tensile Strength, Yield 1600 MPa
232000 psi
when tempered at 1000°F
Elongation at Break 11 %
11 %
when tempered at 1000°F
Reduction of Area 35 %
35 %
when tempered at 1000°F
Modulus of Elasticity 210.3 GPa
30500 ksi
113.8 GPa

@Temperature 649 °C
16510 ksi

@Temperature 1200 °F
191 GPa

@Temperature 343 °C
27700 ksi

@Temperature 649 °F
Charpy Impact 22.0 J
16.2 ft-lb
V Notch, when tempered at 1000°F
Abrasion 128.4
128.4
loss in mm<sup>3</sup>, As-Hardened; ASTM G65
186
186
loss in mm<sup>3</sup>, Tempered at 1200°F; ASTM G65
Thermal Properties Metric English Comments
CTE, linear 11.0 µm/m-°C

@Temperature 27.0 - 93.0 °C
6.11 µin/in-°F

@Temperature 80.6 - 199 °F
13.1 µm/m-°C

@Temperature 27.0 - 649 °C
7.28 µin/in-°F

@Temperature 80.6 - 1200 °F
14.8 µm/m-°C

@Temperature 427 - 788 °C
8.22 µin/in-°F

@Temperature 801 - 1450 °F
Specific Heat Capacity 0.460 J/g-°C
0.110 BTU/lb-°F
Thermal Conductivity 28.6 W/m-K

@Temperature 216 °C
198 BTU-in/hr-ft²-°F

@Temperature 421 °F
Transformation Temperature 818 °C
1500 °F
Ac<sub>1</sub>
Component Elements Properties Metric English Comments
Carbon, C 0.41 %
0.41 %
Chromium, Cr 5.35 %
5.35 %
Iron, Fe 90.59 %
90.59 %
As Balance
Manganese, Mn 0.35 %
0.35 %
Molybdenum, Mo 1.4 %
1.4 %
Silicon, Si 1.0 %
1.0 %
Vanadium, V 0.90 %
0.90 %