- Carpenter Gall-Tough® Stainless, Annealed and Cold Drawn Bar, 10% Cold Work
Carpenter Gall-Tough® Stainless, Annealed and Cold Drawn Bar, 10% Cold Work
| Category | Metal , Ferrous Metal , Stainless Steel , T S20000 Series Stainless Steel |
| Manufacturer | Carpenter Technology Corporation (Cartech) |
| Trade Name | Gall-Tough® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Carpenter Gall-Tough® Stainless, Annealed and Cold Drawn Bar, 10% Cold Work.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Carpenter Technology Corporation.Threshold Galling Stress 103 MPa (higher stress tests not performed). The avg. total volume loss on the wear test is 5 mm³ at 100 rpm.Gall-Tough® stainless is a high silicon, high manganese, nitrogen strengthened, austenitic stainless alloy which possesses superior self-mated galling resistance and metal-to-metal wear resistance. The alloy possesses higher strength and high temperature oxidation resistance than Type 304 stainless with comparable corrosion resistance, depending on the environment.Gall-Tough® is a registered trademark of Carpenter Technology Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.85 g/cc @Temperature 23.0 °C |
0.284 lb/in³ @Temperature 73.4 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 1103 MPa | 160000 psi | |
| 1441 MPa @Temperature -73.0 °C |
209000 psi @Temperature -99.4 °F |
||
| Tensile Strength, Yield | 517 MPa @Strain 0.200 % |
75000 psi @Strain 0.200 % |
|
| 586 MPa @Strain 0.200 %, Temperature -73.0 °C |
85000 psi @Strain 0.200 %, Temperature -99.4 °F |
||
| Elongation at Break | 45 % | 45 % | in 4D |
| 41 % @Temperature -73.0 °C |
41 % @Temperature -99.4 °F |
in 4D | |
| Reduction of Area | 54 % | 54 % | |
| 60 % @Temperature -73.0 °C |
60 % @Temperature -99.4 °F |
||
| Modulus of Elasticity | 171.1 GPa @Temperature 23.0 °C |
24820 ksi @Temperature 73.4 °F |
|
| Charpy Impact | 122 - 224 J | 90.0 - 165 ft-lb | V-notch |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 17.3 µm/m-°C @Temperature 25.0 - 100 °C |
9.60 µin/in-°F @Temperature 77.0 - 212 °F |
|
| 17.73 µm/m-°C @Temperature 25.0 - 250 °C |
9.850 µin/in-°F @Temperature 77.0 - 482 °F |
||
| 18.5 µm/m-°C @Temperature 25.0 - 500 °C |
10.3 µin/in-°F @Temperature 77.0 - 932 °F |
||
| Specific Heat Capacity | 0.5145 J/g-°C @Temperature 52.0 - 102 °C |
0.1230 BTU/lb-°F @Temperature 126 - 216 °F |
|
| Thermal Conductivity | 12.22 W/m-K @Temperature 23.0 °C |
84.81 BTU-in/hr-ft²-°F @Temperature 73.4 °F |
|
| Maximum Service Temperature, Air | 982 °C | 1800 °F | Scaling Temperature for Continuous Service |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.15 % | <= 0.15 % | |
| Chromium, Cr | 15 - 18 % | 15 - 18 % | |
| Iron, Fe | 68 % | 68 % | as remainder |
| Manganese, Mn | 4.0 - 6.0 % | 4.0 - 6.0 % | |
| Molybdenum, Mo | 0.50 - 2.5 % | 0.50 - 2.5 % | |
| Nickel, Ni | 4.0 - 6.0 % | 4.0 - 6.0 % | |
| Nitrogen, N | 0.080 - 0.20 % | 0.080 - 0.20 % | |
| Phosphorous, P | <= 0.040 % | <= 0.040 % | |
| Silicon, Si | 3.0 - 4.0 % | 3.0 - 4.0 % | |
| Sulfur, S | <= 0.040 % | <= 0.040 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000716 ohm-cm @Temperature 23.0 °C |
0.0000716 ohm-cm @Temperature 73.4 °F |