Carlisle 201LL Carbon-Carbon Composite

Category Carbon
Manufacturer Carlisle Brake & Friction
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Carlisle 201LL Carbon-Carbon Composite.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Carbon-Carbon Composite manufactured as sheets from 4mm to 125mm thick this material is essentially a fracture tough, fiber reinforced graphite often referred to as a “CFC”. Good for use in air to 750F (400C) and can be used to 3600F (2000C) when protected by an inert environment or vacuum. Key attributes include thermal shock resistance, fracture toughness, corrosion resistance, electrical conductivity, temperature stability, with a very low coefficient of thermal expansion. Machines quite well with intricate features possible for complex shapes. Common applications include hot glass handling tooling, powdered metal sintering trays, atmosphere and vacuum furnace racks and hardware, spark plasma sintering dies, high temperature nuts, bolts, fasteners, racing brakes and clutches, sputtering targets, and components used in energy production.Information provided by Carlisle Brake & Friction.
Physical Properties Metric English Comments
Apparent Bulk Density 1.65 g/cc
0.0596 lb/in³
Porosity 13 %
13 %
Total
Ash 0.70 %
0.70 %
Mechanical Properties Metric English Comments
Tensile Strength 68.9 MPa
10000 psi
in plane
Modulus of Elasticity 35.9 GPa
5200 ksi
Flexural Strength 103 MPa
15000 psi
perpendicular
138 MPa
20000 psi
in plane
Flexural Modulus 27.6 GPa
4000 ksi
Compressive Strength 68.9 MPa
10000 psi
perpendicular
172 MPa
25000 psi
in plane
Thermal Properties Metric English Comments
CTE, linear 1.90 µm/m-°C

@Temperature 23.0 - 1500 °C
1.06 µin/in-°F

@Temperature 73.4 - 2730 °F
Secant Value
CTE, linear, Transverse to Flow 9.30 µm/m-°C

@Temperature 23.0 - 1500 °C
5.17 µin/in-°F

@Temperature 73.4 - 2730 °F
Secant Value
Specific Heat Capacity 0.850 J/g-°C

@Temperature 50.0 °C
0.203 BTU/lb-°F

@Temperature 122 °F
1.30 J/g-°C

@Temperature 250 °C
0.311 BTU/lb-°F

@Temperature 482 °F
Thermal Conductivity 3.10 W/m-K
21.5 BTU-in/hr-ft²-°F
perpendicular
7.00 W/m-K
48.6 BTU-in/hr-ft²-°F
in plane
Maximum Service Temperature, Air 1500 °C
2730 °F
Electrical Properties Metric English Comments
Electrical Resistivity 0.00387 ohm-cm

@Temperature 17.0 °C
0.00387 ohm-cm

@Temperature 62.6 °F
in plane