CPC - Vycom CELTEC® Expanded Rigid foam PVC board
| Category | Polymer , Thermoplastic , Vinyl (PVC) |
| Manufacturer | CPC - Vycom Co. |
| Trade Name | CELTEC® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CPC - Vycom CELTEC® Expanded Rigid foam PVC board.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Celtec Displayboard is a foamed polyvinyl chloride (PVC) sheet whose combination of features makes it ideal for signage, exhibits, store displays, POP, Kiosks, screen printing and more. The surface is a smooth matte finish that makes it ideal to paint or laminate to secondary substrates. Celtec also has good screw and staple retention which makes it ideal for stage prop design, cabinetry and other wood replacement projects. Sheets are tough, high-strength and lightweight, and can be ordered in a wide range of sizes, thicknesses and colors. Celtec sheets are free of lead, cadmium, barium and zinc. Celtec is recommended for industrial and commercial signage. It readily accepts virtually any form of graphic overlay (print, paint and photo mounting). Celtec is also easy to cut and shape, making it a strong choice for three-dimensional exhibits, displays and stage sets.FEATURES AND BENEFITS Lightweight- Celtec is easy to handle, easy to work with. Low Flammability- Celtec meets UL94 5V, UL 1975 and has a flame spread of 20 according to ASTM E84. Water resistant- Celtec has a closed cell structure and has extremely low water absorption values. Surface- Celtecs smooth matte surface is ideal for graphics, printing and laminating. Weatherability- Celtec is more color-fast than other foam PVC products. Strength- Celtec has an excellent strength to weight ratio as shown in the screw and staple pull test data. Thermal Conductivity- Celtec has excellent insulating characteristics. Safety- Celtec contains no lead, cadmium or zinc.Information provided by Compression Polymers Corp - Vycom
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.550 g/cc @Thickness 10.0 - 25.0 mm |
0.0199 lb/in³ @Thickness 0.394 - 0.984 in |
ASTM D792 |
| 0.700 g/cc @Thickness 1.00 - 6.00 mm |
0.0253 lb/in³ @Thickness 0.0394 - 0.236 in |
ASTM D792 | |
| Water Absorption | 0.15 % @Thickness 10.0 - 25.0 mm |
0.15 % @Thickness 0.394 - 0.984 in |
ASTM D570 |
| 0.30 % @Thickness 1.00 - 6.00 mm |
0.30 % @Thickness 0.0394 - 0.236 in |
ASTM D570 | |
| 0.90 % @Thickness 1.00 - 6.00 mm |
0.90 % @Thickness 0.0394 - 0.236 in |
ASTM D2842 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 15.55 MPa @Thickness 10.0 - 25.0 mm |
2256 psi @Thickness 0.394 - 0.984 in |
ASTM D638 |
| 20.7 MPa @Thickness 1.00 - 6.00 mm |
3000 psi @Thickness 0.0394 - 0.236 in |
ASTM D638 | |
| Tensile Modulus | 0.993 GPa @Thickness 10.0 - 25.0 mm |
144 ksi @Thickness 0.394 - 0.984 in |
ASTM D638 |
| 1.60 GPa @Thickness 1.00 - 6.00 mm |
232 ksi @Thickness 0.0394 - 0.236 in |
ASTM D638 | |
| Flexural Strength | 22.95 MPa @Thickness 10.0 - 25.0 mm |
3329 psi @Thickness 0.394 - 0.984 in |
ASTM D790 |
| Flexural Modulus | 0.9944 GPa @Thickness 10.0 - 25.0 mm |
144.2 ksi @Thickness 0.394 - 0.984 in |
ASTM D790 |
| Izod Impact, Notched | 0.283 J/cm @Thickness 1.00 - 6.00 mm |
0.530 ft-lb/in @Thickness 0.0394 - 0.236 in |
ASTM D256 |
| Charpy Impact, Unnotched | 6.10 J @Thickness 10.0 - 25.0 mm |
4.50 ft-lb @Thickness 0.394 - 0.984 in |
ASTM D256 |
| 11.0 J @Thickness 1.00 - 6.00 mm |
8.10 ft-lb @Thickness 0.0394 - 0.236 in |
ASTM D256 | |
| Gardner Impact | 11.6 J @Thickness 10.0 - 25.0 mm |
8.58 ft-lb @Thickness 0.394 - 0.984 in |
ASTM D4228 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 57.6 µm/m-°C @Thickness 10.0 - 25.0 mm, Temperature 20.0 °C |
32.0 µin/in-°F @Thickness 0.394 - 0.984 in, Temperature 68.0 °F |
ASTM D696 |
| 72.0 µm/m-°C @Thickness 1.00 - 6.00 mm, Temperature 20.0 °C |
40.0 µin/in-°F @Thickness 0.0394 - 0.236 in, Temperature 68.0 °F |
ASTM D696 | |
| Thermal Conductivity | 0.0840 W/m-K @Thickness 1.00 - 6.00 mm |
0.583 BTU-in/hr-ft²-°F @Thickness 0.0394 - 0.236 in |
ASTM C177 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C @Thickness 10.0 - 25.0 mm |
150 °F @Thickness 0.394 - 0.984 in |
ASTM D648 |
| 66.1 °C @Thickness 1.00 - 6.00 mm |
151 °F @Thickness 0.0394 - 0.236 in |
ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 1.00 - 6.00 mm |
V-0 @Thickness 0.0394 - 0.236 in |
5V |
| Flame Spread Index | 20 @Thickness 10.0 - 25.0 mm |
20 @Thickness 0.394 - 0.984 in |
ASTM E84 |
| 20 @Thickness 1.00 - 6.00 mm |
20 @Thickness 0.0394 - 0.236 in |
ASTM E84 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 11.2 kV/mm @Thickness 1.00 - 6.00 mm |
284 kV/in @Thickness 0.0394 - 0.236 in |
ASTM D149 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Burning Rate | No burn when flame removed | |
| Foam Fire | Passed/Classified | UL 1975 |
| Nail Hold, Lbf/in penetration | 35 | ASTM D1761 |
| Oil Canning; (at 140°F) 10mm - 25mm | Passed | ASTM D648 |
| Screw Hold, Lbf/in penetration | 680 | ASTM D1761 |
| Staple Hold, Lbf/in penetration | 180 | ASTM D1761 |