CP-Polymer-Technik Wellamid® 6000 GVZ 45 HWCP 45% Glass Fiber Nylon 6, Impact Resistant, Good Surface Finish, Heat Stabilized, Dry

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled
Manufacturer CP-Polymer-Technik GmbH & Co.
Trade Name Wellamid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF CP-Polymer-Technik Wellamid® 6000 GVZ 45 HWCP 45% Glass Fiber Nylon 6, Impact Resistant, Good Surface Finish, Heat Stabilized, Dry.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by CP-Polymer-Technik GmbH & Co. KG
Physical Properties Metric English Comments
Density 1.50 g/cc
0.0542 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 1.5 - 2.0 %
1.5 - 2.0 %
23°C/50%RH; DIN 53495
Linear Mold Shrinkage 0.0015 cm/cm

@Thickness 4.00 mm
0.0015 in/in

@Thickness 0.157 in
Linear Mold Shrinkage, Transverse 0.0070 cm/cm

@Thickness 4.00 mm
0.0070 in/in

@Thickness 0.157 in
Mechanical Properties Metric English Comments
Tensile Strength at Break 210 MPa
30500 psi
5 mm/min; ISO 527
Elongation at Break 2.5 %
2.5 %
5 mm/min; ISO 527
Tensile Modulus 12.5 GPa
1810 ksi
ISO 527
Flexural Modulus 11.5 GPa
1670 ksi
DIN 52457
Charpy Impact Unnotched 10.0 J/cm²

@Temperature 23.0 °C
47.6 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 2.20 J/cm²

@Temperature 23.0 °C
10.5 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
CTE, linear 15.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
8.33 µin/in-°F

@Temperature 73.4 - 176 °F
DIN 53752
Melting Point 215 °C
419 °F
Kofler
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 179
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
ISO 179
Vicat Softening Point 200 °C
392 °F
50 N; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Stufe; IEC 707
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Stufe; IEC 707
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 93
Surface Resistance 1.00e+12 ohm
1.00e+12 ohm
ISO 3915
Dielectric Constant 4.0

@Frequency 1e+6 Hz
4.0

@Frequency 1e+6 Hz
IEC 250
Dielectric Strength 40.0 kV/mm
1020 kV/in
IEC 243-1
Dielectric Loss Index 0.016
0.016
At 1 MHz; IEC 250
Comparative Tracking Index 550 V
550 V
Stufe; IEC 112
Processing Properties Metric English Comments
Melt Temperature 250 - 280 °C
482 - 536 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Descriptive Properties Value Comments
Back Pressure Low
Holding Pressure High
Injection Speed Medium to High
Screw Speed High