CP-Polymer-Technik Wellamid® 6000 GV 10 HWCP 10% Glass Fiber Nylon 6, Heat Stabilized, Dry

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled
Manufacturer CP-Polymer-Technik GmbH & Co.
Trade Name Wellamid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF CP-Polymer-Technik Wellamid® 6000 GV 10 HWCP 10% Glass Fiber Nylon 6, Heat Stabilized, Dry.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by CP-Polymer-Technik GmbH & Co. KG
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 2.0 - 2.5 %
2.0 - 2.5 %
23°C/50%RH; DIN 53495
Linear Mold Shrinkage 0.0040 cm/cm

@Thickness 4.00 mm
0.0040 in/in

@Thickness 0.157 in
Linear Mold Shrinkage, Transverse 0.010 cm/cm

@Thickness 4.00 mm
0.010 in/in

@Thickness 0.157 in
Mechanical Properties Metric English Comments
Tensile Strength at Break 110 MPa
16000 psi
5 mm/min; ISO 527
Elongation at Break 3.5 %
3.5 %
5 mm/min; ISO 527
Tensile Modulus 5.20 GPa
754 ksi
ISO 527
Flexural Modulus 4.10 GPa
595 ksi
DIN 52457
Charpy Impact Unnotched 4.50 J/cm²

@Temperature 23.0 °C
21.4 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 0.700 J/cm²

@Temperature 23.0 °C
3.33 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
CTE, linear 40.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
22.2 µin/in-°F

@Temperature 73.4 - 176 °F
DIN 53752
Melting Point 215 °C
419 °F
Kofler
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ISO 179
Deflection Temperature at 1.8 MPa (264 psi) 190 °C
374 °F
ISO 179
Vicat Softening Point 200 °C
392 °F
50 N; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Stufe; IEC 707
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Stufe; IEC 707
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 93
Surface Resistance 1.00e+12 ohm
1.00e+12 ohm
ISO 3915
Dielectric Constant 4.0

@Frequency 1e+6 Hz
4.0

@Frequency 1e+6 Hz
IEC 250
Dielectric Strength 35.0 kV/mm
889 kV/in
IEC 243-1
Dielectric Loss Index 0.025
0.025
At 1 MHz; IEC 250
Comparative Tracking Index 550 V
550 V
Stufe; IEC 112
Processing Properties Metric English Comments
Melt Temperature 250 - 280 °C
482 - 536 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Descriptive Properties Value Comments
Back Pressure Low
Holding Pressure High
Injection Speed Medium to High
Screw Speed High