CP-Polymer-Technik Wellamid® 6000 CF 10 HWCP 10% Carbon Fiber Nylon 6, Heat Stabilized, Dry

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Carbon Fiber Filled
Manufacturer CP-Polymer-Technik GmbH & Co.
Trade Name Wellamid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF CP-Polymer-Technik Wellamid® 6000 CF 10 HWCP 10% Carbon Fiber Nylon 6, Heat Stabilized, Dry.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by CP-Polymer-Technik GmbH & Co. KG
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 2.0 - 2.5 %
2.0 - 2.5 %
23°C/50%RH; DIN 53495
Linear Mold Shrinkage 0.0040 cm/cm

@Thickness 4.00 mm
0.0040 in/in

@Thickness 0.157 in
Linear Mold Shrinkage, Transverse 0.010 cm/cm

@Thickness 4.00 mm
0.010 in/in

@Thickness 0.157 in
Mechanical Properties Metric English Comments
Tensile Strength at Break 120 MPa
17400 psi
5 mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 8.50 GPa
1230 ksi
ISO 527
Flexural Modulus 7.50 GPa
1090 ksi
DIN 52457
Charpy Impact Unnotched 3.00 J/cm²

@Temperature 23.0 °C
14.3 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 0.600 J/cm²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
CTE, linear 40.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
22.2 µin/in-°F

@Temperature 73.4 - 176 °F
DIN 53752
Melting Point 215 °C
419 °F
Kofler
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ISO 179
Deflection Temperature at 1.8 MPa (264 psi) 190 °C
374 °F
ISO 179
Vicat Softening Point 200 °C
392 °F
50 N; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Stufe; IEC 707
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Stufe; IEC 707
Electrical Properties Metric English Comments
Volume Resistivity <= 50 ohm-cm
<= 50 ohm-cm
IEC 93
Surface Resistance <= 100 ohm
<= 100 ohm
ISO 3915
Processing Properties Metric English Comments
Melt Temperature 260 - 290 °C
500 - 554 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Descriptive Properties Value Comments
Back Pressure Low
Holding Pressure High
Injection Speed Medium to High
Screw Speed High