C.O.I.M. LARIPUR® LPR6260 PTMG Polyether Polyurethane

Category Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyether Grade
Manufacturer C.O.I.M. S.p.A.
Trade Name Laripur®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF C.O.I.M. LARIPUR® LPR6260 PTMG Polyether Polyurethane.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: The products of the LARIPUR® line are thermoplastic polyurethanes. These products combine the technology of thermoplastic products with the features of polyurethanes:Excellent abrasion resistanceGreat flexibility with constancy at temperature variationsGood compression resistanceGood water and light resistanceGood resistance to oils, fats and to many types of solventsSeries 60 and E 2103 PTMG Ether: These products are based on PTMG polyether. In comparison to the LARIPUR® ester series, they show a higher resistance to hydrolysis and microbiological attacks, have higher cold flexibility but have lower thermal and oxidizing resistance. Information provided by P.A.T. Products, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.17 g/cc
1.17 g/cc
ASTM D792
Mechanical Properties Metric English Comments
Hardness, Shore D 60
60
ASTM D2240
Tensile Strength, Yield 66.4 MPa
9630 psi
ASTM D412
Elongation at Break 380 %
380 %
ASTM D412
50% Modulus 0.0171 GPa
2.48 ksi
ASTM D412
100% Modulus 0.0215 GPa
3.12 ksi
ASTM D412
300% Modulus 0.0442 GPa
6.41 ksi
ASTM D412
Flexural Modulus 0.250 GPa
36.3 ksi
ASTM D790
Izod Impact, Notched (ISO) 9.20 kJ/m²

@Temperature -20.0 °C
4.38 ft-lb/in²

@Temperature -4.00 °F
ASTM D256
Tear Strength 156 kN/m
890 pli
ASTM D624
Abrasion 35
35
mm3, Abrasion Loss; DIN 53516
Torsional Stiffness 56.0 MPa
8120 psi
+20°C; ASTM D1043
252 MPa
36500 psi
-20°C; ASTM D1043
Thermal Properties Metric English Comments
Vicat Softening Point 133 °C
271 °F
ASTM D1525