CLAL-MSX NICLAL 1800 H14 4/4 Hard Copper Alloy, Free Cutting Nickel-Silver
| Category | Metal , Nonferrous Metal , Copper Alloy |
| Manufacturer | CLAL-MSX |
| Trade Name | NICLAL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CLAL-MSX NICLAL 1800 H14 4/4 Hard Copper Alloy, Free Cutting Nickel-Silver.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Main Characteristics: Good corrosion resistanceHigh mechanical propertiesTypical Applications:Parts subject to high stressHigh quality fastenersInformation provided by CLAL-MSX
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.75 g/cc | 0.316 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Vickers | >= 18 | >= 18 | |
| Tensile Strength, Ultimate | 650 - 850 MPa | 94300 - 123000 psi | |
| Tensile Strength, Yield | >= 600 MPa @Strain 0.200 % |
>= 87000 psi @Strain 0.200 % |
|
| Elongation at Break | 3.0 % | 3.0 % | 100 A |
| Modulus of Elasticity | 130 GPa | 18900 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 16.0 µm/m-°C @Temperature 0.000 - 100 °C |
8.89 µin/in-°F @Temperature 32.0 - 212 °F |
|
| Specific Heat Capacity | 0.420 J/g-°C | 0.100 BTU/lb-°F | |
| Thermal Conductivity | 30.0 W/m-K | 208 BTU-in/hr-ft²-°F | |
| Melting Point | 1060 °C | 1940 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Copper, Cu | 62 % | 62 % | |
| Lead, Pb | <= 1.0 % | <= 1.0 % | |
| Nickel, Ni | 18 % | 18 % | |
| Zinc, Zn | <= 19 % | <= 19 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000260 ohm-cm | 0.0000260 ohm-cm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Silvery |