CLAL-MSX NICLAFOR® 1000 TD3 Quenched/Cold Rolled, Rolled Copper Alloy

Category Metal , Nonferrous Metal , Copper Alloy
Manufacturer CLAL-MSX
Trade Name NICLAFOR®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF CLAL-MSX NICLAFOR® 1000 TD3 Quenched/Cold Rolled, Rolled Copper Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeability, good formability, long life duration. Meets environmental concern by not containing Beryllium, Cadmium nor Titanium.Applications:ElectrotechnicElectromechanicElectronicConnecticAutomotiveDomestic appliancesSpectacle industryTurned parts.Information provided by CLAL-MSX
Physical Properties Metric English Comments
Density 8.90 g/cc
0.322 lb/in³
Mechanical Properties Metric English Comments
Hardness, Vickers 200 - 240
200 - 240
Tensile Strength, Ultimate 620 - 720 MPa
89900 - 104000 psi
Tensile Strength, Yield >= 550 MPa

@Strain 0.200 %
>= 79800 psi

@Strain 0.200 %
Elongation at Break >= 3.0 %
>= 3.0 %
A<sub>50 mm</sub>
Modulus of Elasticity 120 GPa
17400 ksi
Modulus of Rigidity 50.0 GPa
7250 ksi
Torsion
Flexural Strength 444 MPa
64400 psi
Rigidty. Elastic bending fatigue, Longitudinal
523 MPa
75900 psi
Rigidty. Elastic bending fatigue, Transverse
Fatigue Strength 450 MPa

@# of Cycles 1.00e+7
65300 psi

@# of Cycles 1.00e+7
Thermal Properties Metric English Comments
CTE, linear 17.25 µm/m-°C

@Temperature 20.0 - 200 °C
9.583 µin/in-°F

@Temperature 68.0 - 392 °F
Thermal Conductivity 53.6 W/m-K
372 BTU-in/hr-ft²-°F
Melting Point 968 - 1078 °C
1770 - 1972 °F
Solidus 968 °C
1770 °F
Liquidus 1078 °C
1972 °F
Component Elements Properties Metric English Comments
Copper, Cu 82.65 - 85.95 %
82.65 - 85.95 %
Iron, Fe <= 0.50 %
<= 0.50 %
Lead, Pb <= 0.030 %
<= 0.030 %
Manganese, Mn 0.050 - 0.30 %
0.050 - 0.30 %
Nickel, Ni 8.5 - 9.5 %
8.5 - 9.5 %
Phosphorous, P <= 0.020 %
<= 0.020 %
Tin, Sn 5.5 - 6.5 %
5.5 - 6.5 %
Zinc, Zn <= 0.50 %
<= 0.50 %
Electrical Properties Metric English Comments
Electrical Resistivity <= 0.00001433 ohm-cm
<= 0.00001433 ohm-cm
precipitation hardened (3h)
<= 0.00001911 ohm-cm
<= 0.00001911 ohm-cm
quenched
Descriptive Properties Value Comments
Bending 0.5
90° bending across and in the rolling direction, longitudinal
0.5
90° bending across and in the rolling direction, transverse