- CIP Composites 100 Series Laminated Polymer Bearing Material
CIP Composites 100 Series Laminated Polymer Bearing Material
| Category | Polymer , Thermoset |
| Manufacturer | CIP Composites |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CIP Composites 100 Series Laminated Polymer Bearing Material.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The 100 series consists of polyester fabric and one of several solid lubricants (optional) in a resin matrix. Non-metallic, high load, high impact and self lubricating laminated material. Laminated polymer material made by impregnating textile with a thermoset resin. CIP Composites™ offer design engineers an attractive, cost effective alternative to the traditional materials used for bushings, bearings, wear pads, and thrust washers, such as bronze, brass or nylon. CIP Composites™ are only 1/6 the weight of steel, easily machined, have good dimensional stability and do not contain harmful or toxic materials.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | |
| Moisture Absorption | <= 0.1 % | <= 0.1 % | water swell < 0.15% |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 100 | 100 | ASTM D785 |
| Tensile Strength | 75.8 MPa | 11000 psi | ASTM D638 |
| Tensile Modulus | 3.24 GPa | 470 ksi | ASTM D638 |
| Flexural Modulus | 1.79 GPa | 260 ksi | ASTM D790 |
| Compressive Yield Strength | 103 MPa | 15000 psi | ASTM D695 |
| Compressive Strength | 93.1 MPa | 13500 psi | Parallel to Laminate; ASTM D695 |
| 345 MPa | 50000 psi | ASTM D695 | |
| Compressive Modulus | 3.45 GPa | 500 ksi | ASTM D695 |
| Poissons Ratio | 0.231 | 0.231 | ASTM D3039-08 |
| Shear Strength | 82.7 MPa | 12000 psi | ASTM D3846 |
| Coefficient of Friction, Dynamic | 0.13 - 0.15 | 0.13 - 0.15 | Dry, Grade CIP 151 (MoS2 + PTFE Filled) |
| 0.15 - 0.20 | 0.15 - 0.20 | Dry, Grade CIP 121 (Graphite Filled) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 32.0 µm/m-°C @Temperature 20.0 - 93.3 °C |
17.8 µin/in-°F @Temperature 68.0 - 200 °F |
Parallel to Laminate |
| CTE, linear, Transverse to Flow | 63.0 µm/m-°C @Temperature 20.0 - 93.3 °C |
35.0 µin/in-°F @Temperature 68.0 - 200 °F |
Normal to Laminate |
| Maximum Service Temperature, Air | 93.3 °C | 200 °F | |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.20e+15 ohm-cm | 4.20e+15 ohm-cm | ASTM D257-07 |
| Dielectric Strength | 7.87 kV/mm | 200 kV/in | ASTM D149-97a |