Bulk Molding Compounds BMC 404 Thermoset Polyester, Low Shrink, High Strength, Electrical Grade

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Polyester, TS , Thermoset Polyester Glass Filled BMC
Manufacturer	BMC - Bulk Molding Compounds Inc.
Trade Name	BMC
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Bulk Molding Compounds BMC 404 Thermoset Polyester, Low Shrink, High Strength, Electrical Grade.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

BMC 404 is a high strength, low shrink, glass reinforced polyester molding compound that meets Ford Specification ESF-M3D121-A. BMC 404 has excellent electrical properties and creep resistance. It can be pigmented in a wide range of colors and can be supplied in bulk or extruded in pre -weighed slugs.Typical applications are injection, compression or transfer molded circuit breakers, insulators, and power tool housings.

Physical Properties	Metric	English	Comments
Specific Gravity	1.80 - 1.90 g/cc	1.80 - 1.90 g/cc
Water Absorption	0.12 - 0.20 %	0.12 - 0.20 %	24 hours, 23°C
Linear Mold Shrinkage	0.0015 - 0.0040 cm/cm	0.0015 - 0.0040 in/in

Mechanical Properties	Metric	English
Hardness, Barcol	45 - 55	45 - 55
Tensile Strength, Ultimate	37.9 - 55.2 MPa	5500 - 8000 psi
Flexural Strength	103 - 124 MPa	15000 - 18000 psi
Flexural Modulus	11.0 - 13.1 GPa	1600 - 1900 ksi
Compressive Strength	124 - 145 MPa	18000 - 21000 psi
Izod Impact, Notched	2.67 - 4.81 J/cm	5.00 - 9.00 ft-lb/in

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	>= 260 °C	>= 500 °F
Flammability, UL94	V-0	V-0

Electrical Properties	Metric	English	Comments
Dielectric Strength	13.8 - 14.6 kV/mm	350 - 370 kV/in	Short Time
Arc Resistance	>= 180 sec	>= 180 sec
Comparative Tracking Index	>= 500 V	>= 500 V

Processing Properties	Metric	English	Comments
Mold Temperature	138 - 166 °C	280 - 330 °F