Braskem ML3601U LLDPE Rotomolding Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Rotational Molding Grade
Manufacturer Braskem
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Braskem ML3601U LLDPE Rotomolding Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The resin ML3601U is a linear low-density polyethylene, 1-hexene based, with excellent environmental stress cracking resistance and high impact strength. It contains long term UV8 stabilization and antioxidant additives. This resin is ideally suited for applications that require a higher mechanical performance. This resin was especially developed to produce rotomolded large tanks for water and chemical products storage, underground tanks, septic tanks, and manholes. This resin is recommended for rotational molding under conditions comparable to polyethylene resins with a similar melt index and density range. Oven temperature range: 180 to 350 ºC.
Physical Properties Metric English Comments
Density 0.939 g/cc
0.0339 lb/in³
ASTM-D1505
ESCR 100% Igepal® >= 1000 hour

@Thickness 2.00 mm,
Temperature 50.0 °C
>= 1000 hour

@Thickness 0.0787 in,
Temperature 122 °F
0.3 mm notched-plaques; ASTM-D1693
ESCR 10% Igepal® 145 hour

@Thickness 2.00 mm,
Temperature 50.0 °C
145 hour

@Thickness 0.0787 in,
Temperature 122 °F
0.3 mm notched-plaques; ASTM-D1693
Melt Flow 3.3 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.3 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM-D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 30.1 MPa
4370 psi
ASTM-D638
Tensile Strength, Yield 21.0 MPa
3050 psi
ASTM-D638
Elongation at Break >= 1000 %
>= 1000 %
ASTM-D638
Elongation at Yield 14 %
14 %
ASTM-D638
Flexural Modulus, 1% Secant 760 MPa
110000 psi
ASTM-D790
Impact Test 82.0 J

@Thickness 3.17 mm,
Temperature -40.0 °C
60.5 ft-lb

@Thickness 0.125 in,
Temperature -40.0 °F
ARM
228 J

@Thickness 6.34 mm,
Temperature -40.0 °C
168 ft-lb

@Thickness 0.250 in,
Temperature -40.0 °F
ARM
Thermal Properties Metric English Comments
Melting Point 127 °C
261 °F
ASTM-D3418
Deflection Temperature at 0.46 MPa (66 psi) 60.0 °C
140 °F
ASTM-D648
Deflection Temperature at 1.8 MPa (264 psi) 41.0 °C
106 °F
ASTM-D648