Braskem LL6801N LLDPE Blown Film Extrusion Polyethylene Copolymer

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Octene, Film
Manufacturer Braskem
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Braskem LL6801N LLDPE Blown Film Extrusion Polyethylene Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The LL6801N resin is a linear low-density polyethylene, copolymer of octene-1, produced by the solution process for blown film extrusion with excellent mechanical properties. It contains processing aid, slip, antiblock, and antioxidant additives. Its applications range from high performance films to automatic packaging of solid and liquids and include lamination and coextrusion. The LL6801N resin should be processed on specific extruders for LLDPE. The best results are obtained at a melt temperature within the range of 200 to 220ºC. Recommended blow up ratio: 2.4 to 3.0:1.
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
ASTM-D792
Melt Flow 0.75 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.75 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM-D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 940 %
940 %
ASTM-D882
Film Elongation at Break, TD 1260 %
1260 %
ASTM-D882
Elmendorf Tear Strength MD 350 g
350 g
ASTM-D1922
Elmendorf Tear Strength TD 780 g
780 g
ASTM-D1922
Elmendorf Tear Strength, MD 14.0 g/micron
356 g/mil
ASTM-D1922
Elmendorf Tear Strength, TD 31.2 g/micron
792 g/mil
ASTM-D1922
Dart Drop 9.20 g/micron
234 g/mil
ASTM-D1709
Dart Drop Test 230 g
0.507 lb
ASTM-D1709
Film Tensile Strength at Break, MD 40.0 MPa
5800 psi
ASTM-D882
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM-D882
1% Secant Modulus, MD 150 MPa
21800 psi
ASTM-D882
1% Secant Modulus, TD 180 MPa
26100 psi
ASTM-D882
Optical Properties Metric English Comments
Haze 9.0 %
9.0 %
ASTM-D1003
Gloss 113 %
113 %
Angle 60°; ASTM-D2457