Braskem LL5800N LLDPE Blown Film Extrusion Polyethylene Copolymer

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Octene, Film
Manufacturer Braskem
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Braskem LL5800N LLDPE Blown Film Extrusion Polyethylene Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LL5800N resin is a linear low-density polyethylene, copolymer of octene-1, produced by the solution process for blown film extrusion with excellent mechanical properties. It contains processing aid and antioxidant additives. Its applications include: heavy-duty bags, stretch liners, LDPE and HDPE blends, and packages for general use. LL5800N resin should be processed on specific extruders for LLDPE. The best results are obtained at a melt temperature within the range of 200 to 220º and blends with LDPE with a maximum ratio of 30%. Recommended blow up ratio: 1.8 to 3:1.
Physical Properties Metric English Comments
Density 0.918 g/cc
0.0332 lb/in³
ASTM-D792
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM-D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 920 %
920 %
ASTM-D882
Film Elongation at Break, TD 1240 %
1240 %
ASTM-D882
Elmendorf Tear Strength MD 330 g
330 g
ASTM-D1922
Elmendorf Tear Strength TD 770 g
770 g
ASTM-D1922
Elmendorf Tear Strength, MD 13.2 g/micron
335 g/mil
ASTM-D1922
Elmendorf Tear Strength, TD 30.8 g/micron
782 g/mil
ASTM-D1922
Dart Drop 8.00 g/micron
203 g/mil
ASTM-D1709
Dart Drop Test 200 g
0.441 lb
ASTM-D1709
Film Tensile Strength at Break, MD 50.0 MPa
7250 psi
ASTM-D882
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM-D882
1% Secant Modulus, MD 150 MPa
21800 psi
ASTM-D882
1% Secant Modulus, TD 170 MPa
24700 psi
ASTM-D882
Optical Properties Metric English Comments
Haze 8.0 %
8.0 %
ASTM-D1003
Gloss 121 %
121 %
Angle 60°; ASTM-D2457