Braskem LH537 LLDPE Cast Film Extrusion Polyethylene

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade
Manufacturer	Braskem
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Braskem LH537 LLDPE Cast Film Extrusion Polyethylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LH537 is a LLDPE Hexene produced by Braskem. It offers an excellent processability, stiffness, and soft touch for flat die films. It has very low gel contents. It contains slip absent and antiblock absent additives. Its applications include diapers (back sheet) and absorbent pads (back sheet).

Physical Properties	Metric	English	Comments
Density	0.937 g/cc	0.0339 lb/in³	ASTM-D792
Melt Flow	4.8 g/10 min @Load 2.16 kg, Temperature 190 °C	4.8 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM-D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	1320 %	1320 %	ASTM-D882
Film Elongation at Break, TD	1400 %	1400 %	ASTM-D882
Elmendorf Tear Strength MD	20 g	20 g	ASTM-D1922
Elmendorf Tear Strength TD	30 g	30 g	ASTM-D1922
Film Tensile Strength at Break, MD	30.0 MPa	4350 psi	ASTM-D882
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ASTM-D882
1% Secant Modulus, MD	420 MPa	60900 psi	ASTM-D882
1% Secant Modulus, TD	430 MPa	62400 psi	ASTM-D882

Optical Properties	Metric	English	Comments
Gloss	9.0 %	9.0 %	Angle 60°; ASTM-D2457

Descriptive Properties	Value	Comments
Mass Temperature (°C)	230-250	Cast Films
Screen Package	40/40	mesh, 100% pure
	40/60/40	mesh, Blend
Temperature Profile (°C)	190-230	Cast Films