Braskem Idealis 500 Compression Molding High Molecular Weight Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), UHMW PE Ultra High Molecular Weight
Manufacturer Braskem
Trade Name Idealis
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Braskem Idealis 500 Compression Molding High Molecular Weight Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Braskem Idealis 500 is the only high molecular weight polyethylene resin in powder form specially designed for the compression molding process. Its applications range from food handling, cutting boards, and playground toys to technical parts.
Physical Properties Metric English Comments
Density 0.951 g/cc
0.0344 lb/in³
ASTM-D792
Apparent Bulk Density 0.450 g/cc
0.0163 lb/in³
ASTM-D1895
Particle Size 170 µm
170 µm
Average, Dp50; ASTM-D1921
Viscosity Test 470 cm³/g
470 cm³/g
Intrinsic; ASTM-D4020
Molecular Weight 550000 g/mol
550000 g/mol
Melt Flow 0.70 g/10 min

@Load 21.6 kg,
Temperature 190 °C
0.70 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ASTM-D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 63
63
15 sec; ASTM-D2240
Tensile Strength at Break >= 30.0 MPa
>= 4350 psi
ASTM-D638 / ISO 527
Tensile Strength, Yield >= 20.0 MPa
>= 2900 psi
ASTM-D638 / ISO 527
Elongation at Break >= 500 %
>= 500 %
ASTM-D638 / ISO 527
Flexural Modulus 0.930 GPa
135 ksi
ASTM-D790
Charpy Impact, Notched >= 5.00 J/cm²
>= 23.8 ft-lb/in²
double-notched specimens (14° v-notch on both sides); ISO 11542-2
Sand Slurry 80
80
Sand slurry - Internal, reference PE500 = 100
Thermal Properties Metric English Comments
Melting Point 136 °C
277 °F
ASTM-D3418
Vicat Softening Point 80.0 °C

@Load 5.10 kg
176 °F

@Load 11.2 lb
ASTM-D1525