Braskem HB0454 HDPE Blow Molding Polyethylene Copolymer

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer Braskem
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Braskem HB0454 HDPE Blow Molding Polyethylene Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
HB0454 is a high-density polyethylene copolymer resin with average molecular weight produced by the Unipol® process. A bottle made with HB0454 shows excellent processability, color, and superficial appearance, good chemical resistance, resistance to piling up, and does not have residual odor. Barbs can be detached easily since it has also been adjusted for use in high productivity rotating machines. Its applications include: small medicine bottles and bottles for cleaning products, cosmetics, food products, and tensioactive products.
Physical Properties Metric English Comments
Density 0.954 g/cc
0.0345 lb/in³
ASTM-D792
ESCR 100% Igepal® 46 hour

@Thickness 2.00 mm,
Temperature 50.0 °C
46 hour

@Thickness 0.0787 in,
Temperature 122 °F
0.3 mm notched-plaques; ASTM-D1693
ESCR 10% Igepal® 23 hour

@Thickness 2.00 mm,
Temperature 50.0 °C
23 hour

@Thickness 0.0787 in,
Temperature 122 °F
0.3 mm notched-plaques; ASTM-D1693
Melt Flow 0.36 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.36 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM-D1238
32 g/10 min

@Load 21.6 kg,
Temperature 190 °C
32 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ASTM-D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 59
59
ASTM-D2240
Tensile Strength at Break 31.0 MPa
4500 psi
ASTM-D638
Tensile Strength, Yield 29.0 MPa
4210 psi
ASTM-D638
Flexural Modulus, 1% Secant 1010 MPa
146000 psi
ASTM-D790
Izod Impact, Notched 1.09 J/cm
2.04 ft-lb/in
ASTM-D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 69.0 °C
156 °F
ASTM-D648
Vicat Softening Point 127 °C

@Load 1.02 kg
261 °F

@Load 2.25 lb
ASTM-D1525