Braskem Green PE SLL318 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene

Category Polymer , Film , Renewable/Recycled Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer Braskem
Trade Name Green PE
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Braskem Green PE SLL318 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: SLL118 is a Linear Low Density Polyethylene, copolymer of butene-1. Developed for blown film extrusion in blends with polyethylenes. Films obtained with this product show a good processing performance balanced with good optical and mechanical properties as well as sealability. Very low gel amount. It contains antioxidant additives. The minimum biobased content of this grade is 87%, determined according to ASTM D6866. Applications: Stretch films; liners; LDPE and HDPE blends and packages for general use. Others applications: blends for irrigation pipes.Information provided by Braskem.
Physical Properties Metric English Comments
Specific Gravity 0.918 g/cc
0.918 g/cc
ASTM D1505/D792
Thickness 25.0 microns
0.984 mil
Melt Flow 2.7 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.7 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 1220 %
1220 %
ASTM D882
Film Elongation at Break, TD 1440 %
1440 %
ASTM D882
Elmendorf Tear Strength MD 120 g
120 g
gF; ASTM D1922
Elmendorf Tear Strength TD 340 g
340 g
gF; ASTM D1922
Dart Drop Test 90.0 g
0.198 lb
g/F50; ASTM D1709
Film Tensile Strength at Break, MD 30.0 MPa
4350 psi
ASTM D882
Film Tensile Strength at Break, TD 30.0 MPa
4350 psi
ASTM D882
1% Secant Modulus, MD 180 MPa
26100 psi
ASTM D882
1% Secant Modulus, TD 200 MPa
29000 psi
ASTM D882