Braskem Green PE SLH218 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene

Category	Polymer , Film , Renewable/Recycled Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer	Braskem
Trade Name	Green PE
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Braskem Green PE SLH218 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: SLH218 is a LLDPE Hexene copolymer produced by Braskem. It shows a good balance between optical properties, mechanical properties (Mainly stretchability), sealability and processability. Very low gel contained. The minimum biobased content of this grade is 84%, determined according to ASTM D6866. Additive: Slip Absent; Antiblock Absent Applications: Stretch films; Liners; LDPE and HDPE blends; packages for general use; Others applications: insulation for low and medium tension XLPE wires and cables; blends for irrigation pipes.Information provided by Braskem.

Physical Properties	Metric	English	Comments
Specific Gravity	0.916 g/cc	0.916 g/cc	ASTM D1505/D792
Thickness	25.0 microns	0.984 mil
Melt Flow	2.3 g/10 min @Load 2.16 kg, Temperature 190 °C	2.3 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	1170 %	1170 %	ASTM D882
Film Elongation at Break, TD	1500 %	1500 %	ASTM D882
Elmendorf Tear Strength MD	240 g	240 g	gF; ASTM D1922
Elmendorf Tear Strength TD	520 g	520 g	gF; ASTM D1922
Dart Drop Test	110 g	0.243 lb	g/F50; ASTM D1709
Film Tensile Strength at Break, MD	40.0 MPa	5800 psi	ASTM D882
Film Tensile Strength at Break, TD	40.0 MPa	5800 psi	ASTM D882
1% Secant Modulus, MD	210 MPa	30500 psi	ASTM D882
1% Secant Modulus, TD	240 MPa	34800 psi	ASTM D882