- Braskem Green PE SGM9450F Blow Film Extrusion and Cast Film Extrusion High Density Polyethylene
Braskem Green PE SGM9450F Blow Film Extrusion and Cast Film Extrusion High Density Polyethylene
| Category | Polymer , Film , Renewable/Recycled Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade |
| Manufacturer | Braskem |
| Trade Name | Green PE |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Braskem Green PE SGM9450F Blow Film Extrusion and Cast Film Extrusion High Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: SGM9450F is a high-density polyethylene, developed for the high molecular weight film extrusion segment produced with bimodal technology. The film produced from this resin has high tenacity and excellent resistance to impact characteristics. This resin has wide molar mass distribution that makes it easier to process. The minimum biobased content of this grade is 96%, determined according to ASTM D6866. Application: Bags in general (like T-shirt bags, Handle Bags, Star Bags, others); Geomembranes.Information provided by Braskem.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.952 g/cc | 0.952 g/cc | ASTM D1505/D792 |
| Thickness | 12.5 microns | 0.492 mil | |
| Melt Flow | 0.33 g/10 min @Load 5.00 kg, Temperature 190 °C |
0.33 g/10 min @Load 11.0 lb, Temperature 374 °F |
ASTM D1238 |
| 9.3 g/10 min @Load 21.6 kg, Temperature 190 °C |
9.3 g/10 min @Load 47.6 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 590 % | 590 % | ASTM D882 |
| Film Elongation at Break, TD | 740 % | 740 % | ASTM D882 |
| Elmendorf Tear Strength MD | 58 g | 58 g | gF; ASTM D1922 |
| Elmendorf Tear Strength TD | 51 g | 51 g | gF; ASTM D1922 |
| Dart Drop Test | 245 g | 0.540 lb | g/F50; ASTM D1709 |
| Film Tensile Strength at Break, MD | 85.0 MPa | 12300 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 45.0 MPa | 6530 psi | ASTM D882 |
| Heat Seal Strength Initiation Temperature | 125 °C | 257 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Puncture Strength | 80 J/m |