Braskem GM9450F HDPE Blown Film Extrusion Polyethylene

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer	Braskem
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Braskem GM9450F HDPE Blown Film Extrusion Polyethylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

HDPE GM9450F is a high-density polyethylene developed for the high molecular weight film extrusion segment produced with bimodal technology. The film produced from this resin has high tenacity and excellent resistance to impact characteristics. This resin has wide molar mass distribution that makes it easier to process. Its applications include: retail bags, perforated rolls, repackaging, geomembranes, and bags in general.

Physical Properties	Metric	English	Comments
Density	0.952 g/cc	0.0344 lb/in³	ASTM-D792
Melt Flow	0.33 g/10 min @Load 5.00 kg, Temperature 190 °C	0.33 g/10 min @Load 11.0 lb, Temperature 374 °F	ASTM-D1238
	9.3 g/10 min @Load 21.6 kg, Temperature 190 °C	9.3 g/10 min @Load 47.6 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	40.0 MPa	5800 psi	ASTM-D882
Film Tensile Strength at Yield, TD	30.0 MPa	4350 psi	ASTM-D882
Film Elongation at Break, MD	620 %	620 %	ASTM-D882
Film Elongation at Break, TD	680 %	680 %	ASTM-D882
Elmendorf Tear Strength MD	6.0 g	6.0 g	ASTM-D1922
Elmendorf Tear Strength TD	60 g	60 g	ASTM-D1922
Dart Drop Test	210 g	0.463 lb	ASTM-D1709
Film Tensile Strength at Break, MD	40.0 MPa	5800 psi	ASTM-D882
Film Tensile Strength at Break, TD	50.0 MPa	7250 psi	ASTM-D882
Heat Seal Strength Initiation Temperature	125 °C	257 °F	Braskem Method

Descriptive Properties	Value	Comments
Puncture Strength (J/m)	80	Braskem Method