Braskem GM5010T2B HDPE High Density Extrusion Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Pipe Grade
Manufacturer Braskem
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Braskem GM5010T2B HDPE High Density Extrusion Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
GM5010T2B is a high-density polyethylene compound specially developed for the manufacturing of extruded pipes for water distribution. It is produced with bimodal technology and has high molar mass. It shows high mechanical properties and has excellent resistance to hydrostatic pressure and to stress cracking. This resin has the MRS (Minimum Required Strength) of 8 MPa, according to ISO 9080, and is classified as PE 80 according to ISO 12162. GM5010T2B is manufactured in a blue color and contains additives to protect it against ultraviolet radiation action and photodegradation. Its applications include blue PE 80 pressure pipes for water branch lines for buildings and distribution and adductors water systems.
Physical Properties Metric English Comments
Density 0.947 g/cc
0.0342 lb/in³
ASTM-D792
ESCR 100% Igepal® >= 1000 hour

@Thickness 2.00 mm,
Temperature 50.0 °C
>= 1000 hour

@Thickness 0.0787 in,
Temperature 122 °F
0.3 mm notched-plaques; ASTM-D1693
Melt Flow 0.45 g/10 min

@Load 5.00 kg,
Temperature 190 °C
0.45 g/10 min

@Load 11.0 lb,
Temperature 374 °F
ASTM-D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 62
62
ASTM-D2240
Tensile Strength at Break 36.0 MPa
5220 psi
ASTM-D638
Tensile Strength, Yield 22.0 MPa
3190 psi
ASTM-D638
Elongation at Break 910 %
910 %
ASTM-D638
Elongation at Yield 12 %
12 %
ASTM-D638
Flexural Modulus, 1% Secant 1090 MPa
158000 psi
ASTM-D790
Izod Impact, Notched 2.60 J/cm
4.87 ft-lb/in
ASTM-D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 69.0 °C
156 °F
ASTM-D648
Vicat Softening Point 122 °C

@Load 1.02 kg
252 °F

@Load 2.25 lb
ASTM-D1525