Braskem CP 191 Injection Molding Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | Braskem |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Braskem CP 191 Injection Molding Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Household; low temperature packing; frozen desserts packaging. Information provided by Braskem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in³ | ASTM D792A |
| Melt Flow | 80 g/10 min @Load 2.16 kg, Temperature 230 °C |
80 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238L |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 58 | 58 | ASTM D785 |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Modulus | 1.00 GPa | 145 ksi | ASTM D790 |
| Izod Impact, Notched | 0.400 J/cm @Temperature -20.0 °C |
0.749 ft-lb/in @Temperature -4.00 °F |
ASTM D256A |
| 0.630 J/cm @Temperature 23.0 °C |
1.18 ft-lb/in @Temperature 73.4 °F |
ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 53.0 °C | 127 °F | ASTM D648 |
| Vicat Softening Point | 137 °C | 279 °F | -1kg; ASTM D1525 |
Users viewing this material also viewed the following:
- MV Labs DY200 DyBr3·xH2O Dysprosium bromide hydrate
- Zircar Zirconia FBD Zirconia Boards, Discs, and Cylinders Insulation
- LyondellBasell Petrothene® NA334000 Low Density Polyethylene
- Huntsman AroCy B-40S Prepolymer Bisphenol-A Dicyanate
- Haynes 556® alloy, 50% cold reduction, 1010°C anneal for 5 minutes
- Chase Plastics CP Pryme® NN300L (DAM) Nylon 66 (Utility Grade), Internally Lubricated
- Tisan TISSAN® UNR Styrene Acrylonitrile
- A. Schulman POLYFLAM™ RCP 505C Flame Retardant Concentrate Based In Low-Density Polyethylene
- Fainplast Compounds CTS 84 Flexible PVC, Extrusion Modified with Rubber
Copyright © lookpolymers.com All Rights Reserved