Braskem BF 0323 HC LDPE Blown Film Extrusion Polyethylene

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer	Braskem
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Braskem BF 0323 HC LDPE Blown Film Extrusion Polyethylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: BF0323HC is a high molecular weight grade produced under high pressure. Films obtained with this product show excellent mechanical and optical properties38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Heavy duty bags; agricultural films; shrink films for pallets. Information provided by Braskem

Physical Properties	Metric	English	Comments
Density	0.923 g/cc	0.0333 lb/in³	ASTM D1505
Thickness	38.0 microns	1.50 mil
Melt Flow	0.32 g/10 min @Load 2.16 kg, Temperature 230 °C	0.32 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	390 %	390 %	ASTM D882
Film Elongation at Break, TD	1040 %	1040 %	ASTM D882
Elmendorf Tear Strength, TD	90.0 g/micron	2290 g/mil	ASTM D1922
Dart Drop	100 g/micron	2540 g/mil	F50; ASTM D1709
Film Tensile Strength at Break, MD	40.0 MPa	5800 psi	ASTM D882
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ASTM D882

Optical Properties	Metric	English	Comments
Haze	10 %	10 %	ASTM D1003
Gloss	72 %	72 %	60° angle; ASTM D2457

Descriptive Properties	Value	Comments
Minimum Recommended Thickness	50 µm