Borealis Xmod™ K65G2 20% Glass Fiber Reinforced Polypropylene Compound

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler
Manufacturer Borealis
Trade Name Xmod™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Xmod™ K65G2 20% Glass Fiber Reinforced Polypropylene Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Xmod K65G2 is a 20% glass fiber reinforced grade intended for injection molding. Xmod K65G2 has been developed especially for the car industry, to be used UTB parts. Xmod K65G2 offers good balance in stiffness/impact strength.Xmod K65G2 has been designed for automotive UTB parts.Information provided by the Manufacturer.
Physical Properties Metric English Comments
Density 1.06 g/cc
0.0383 lb/in³
ISO 1183
Melt Flow 7.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
7.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
34 g/10 min

@Load 5.00 kg,
Temperature 230 °C
34 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 124 MPa
18000 psi
H 385/30; ISO 2039
Tensile Strength, Yield 86.0 MPa
12500 psi
At 50 mm/min; ISO 527-2
Elongation at Yield 3.0 %
3.0 %
At 50 mm/min; ISO 527-2
Flexural Modulus 4.40 GPa
638 ksi
At 2 mm/min; ISO 178
Charpy Impact Unnotched 4.10 J/cm²
19.5 ft-lb/in²
ISO 179/1eU
2.50 J/cm²

@Temperature -20.0 °C
11.9 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
ISO 179/1eA
0.570 J/cm²

@Temperature -20.0 °C
2.71 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 145 °C
293 °F
ISO 75-2
Vicat Softening Point 132 °C
270 °F
B (50N); ISO 306
165 °C
329 °F
A (10N); ISO 306
Processing Properties Metric English Comments
Melt Temperature 210 - 260 °C
410 - 500 °F
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F
Descriptive Properties Value Comments
Fogging, mg 2.3
At 100°C/ 16 hours