Borealis Xmod™ HF006SA High Stiffness Polypropylene for Injection Molding Applications
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | Borealis |
| Trade Name | Xmod™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Borealis Xmod™ HF006SA High Stiffness Polypropylene for Injection Molding Applications.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Xmod HF006SA is a high melt flow PP homopolymer with increased crystallinity, intended for injection molding. Xmod HF006SA is specifically developed for applications demanding a high surface appearance and high stiffness. Xmod HF006SA is equipped for very good long term heat resistance, show excellent antistatic performance and meets the requirements for food contact regulations.Xmod HF006SA is intended for household applications like irons, coffee makers, fryers, food mixers, control panels washing appliances, and external panels refrigerators.Information provided by the Manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ISO 1183 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 90.0 MPa | 13100 psi | H 385/30; ISO 2039 |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 2.10 GPa | 305 ksi | At 1 mm/min; ISO 527-2 |
| Flexural Modulus | 2.00 GPa | 290 ksi | At 5 mm/min; ISO 178 |
| Charpy Impact, Notched | 0.250 J/cm² | 1.19 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 121 °C | 250 °F | ISO 75-2 |
| Vicat Softening Point | 158 °C | 316 °F | A (10N); ISO 306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 82 % @Thickness 2.00 mm |
82 % @Thickness 0.0787 in |
20°, plaque; DIN 67530 |
| 90 % @Thickness 2.00 mm |
90 % @Thickness 0.0787 in |
60°, 2 mm plaque; DIN 67530 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | Polymer Mass Temp |
| Mold Temperature | 30.0 - 60.0 °C | 86.0 - 140 °F |