Borealis RA130E Polypropylene Random Copolymer

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer
Manufacturer Borealis
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis RA130E Polypropylene Random Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
RA130E is a high molecular weight, low melt flow rate polypropylene random copolymer (PP-R) compound and is natural colored. Applications RA130E is recommended for the production of PP-R pipes and fittings used in heating, plumbing, domestic water, relining, and industrial applications. The product is used for single as well as for multilayer pipes, where you then differentiate between plastic multilayer and aluminum multilayer pipes. Specifications: DIN 8078; DIN 8077; and EN ISO 15874.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 0.905 g/cc
0.0327 lb/in³
ISO 1183
Melt Flow 0.25 g/10 min

@Load 2.16 kg,
Temperature 230 °C
0.25 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 25.0 MPa
3630 psi
50mm/min; ISO 527-2
Elongation at Yield 13.5 %
13.5 %
50mm/min; ISO 527-2
Tensile Modulus 0.900 GPa
131 ksi
1mm/min; ISO 527
Flexural Modulus 0.800 GPa
116 ksi
2mm/min; ISO 178
Charpy Impact Unnotched 4.00 J/cm²

@Temperature -20.0 °C
19.0 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eU
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
NB

@Temperature 0.000 °C
NB

@Temperature 32.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.200 J/cm²

@Temperature -20.0 °C
0.952 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
0.350 J/cm²

@Temperature 0.000 °C
1.67 ft-lb/in²

@Temperature 32.0 °F
ISO 179/1eA
2.00 J/cm²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 150 µm/m-°C

@Temperature 0.000 - 70.0 °C
83.3 µin/in-°F

@Temperature 32.0 - 158 °F
DIN 53752
Thermal Conductivity 0.240 W/m-K
1.67 BTU-in/hr-ft²-°F
DIN 52612
Processing Properties Metric English Comments
Middle Barrel Temperature 180 - 210 °C
356 - 410 °F
Die Temperature 210 - 220 °C
410 - 428 °F
Melt Temperature 220 °C
428 °F
Head Temperature 210 - 220 °C
410 - 428 °F