Borealis RA130E-6017 Polypropylene Random Copolymer

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer
Manufacturer Borealis
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis RA130E-6017 Polypropylene Random Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
RA130E-6017 is a high molecular weight, low melt flow rate polypropylene random copolymer (PP-R) compound and is green colored. Applications: domestic water, heating, relining, plumbing, and industrial applications. Specifications: DIN 8078; DIN 8077; and EN ISO 15874.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 0.905 g/cc
0.0327 lb/in³
ISO 1183
Melt Flow 0.30 g/10 min

@Load 2.16 kg,
Temperature 230 °C
0.30 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 25.0 MPa
3630 psi
50mm/min; ISO 527-2
Elongation at Yield 13.5 %
13.5 %
50mm/min; ISO 527-2
Tensile Modulus 0.900 GPa
131 ksi
1mm/min; ISO 527
Flexural Modulus 0.800 GPa
116 ksi
2mm/min; ISO 178
Charpy Impact Unnotched 4.00 J/cm²

@Temperature -20.0 °C
19.0 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eU
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
NB

@Temperature 0.000 °C
NB

@Temperature 32.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.200 J/cm²

@Temperature -20.0 °C
0.952 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
0.350 J/cm²

@Temperature 0.000 °C
1.67 ft-lb/in²

@Temperature 32.0 °F
ISO 179/1eA
2.00 J/cm²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 150 µm/m-°C

@Temperature 0.000 - 70.0 °C
83.3 µin/in-°F

@Temperature 32.0 - 158 °F
DIN 53752
Thermal Conductivity 0.240 W/m-K
1.67 BTU-in/hr-ft²-°F
DIN 52612
Processing Properties Metric English Comments
Middle Barrel Temperature 180 - 210 °C
356 - 410 °F
cylinder
Die Temperature 210 - 220 °C
410 - 428 °F
Melt Temperature 210 - 220 °C
410 - 428 °F
Head Temperature 210 - 220 °C
410 - 428 °F