Borealis PS65C40 Polypropylene Compound, Mineral Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Borealis |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Borealis PS65C40 Polypropylene Compound, Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PS65C40 is a 40% mineral filled polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness, gives a good surface quality and is easy to process. Applications: PS65C40 has been developed especially for applications like: washing machine parts, and household applications.Information provided by Borealis AG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | average process; in flow; 150x80x2mm |
| 0.010 cm/cm | 0.010 in/in | average process; cross flow; 150x80x2mm | |
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 230 °C |
16 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | 50mm/min; ISO 527-2 |
| Tensile Modulus | 2.80 GPa | 406 ksi | 1mm/min; ISO 527-2 |
| Flexural Modulus | 2.60 GPa | 377 ksi | 2mm/min; ISO 178 |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.210 J/cm² @Temperature 23.0 °C |
0.999 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 °C | 144 °F | ISO 75-2 |
| Vicat Softening Point | 105 °C @Load 5.10 kg |
221 °F @Load 11.2 lb |
ISO 306 |
| 155 °C @Load 1.02 kg |
311 °F @Load 2.25 lb |
ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 220 - 260 °C | 428 - 500 °F | mass temperature |
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |
| Injection Velocity | 100 - 200 mm/sec | 3.94 - 7.87 in/sec | |
| Hold Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | low to medium | |
| Screw Speed | low to medium |