Borealis LE0516 Polyethylene Compound, Crosslinkable, Semiconductive

Category	Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer	Borealis
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Borealis LE0516 Polyethylene Compound, Crosslinkable, Semiconductive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LE0516 is a crosslinkable black polyethylene compound, specially designed for strippable semi conductive screen applications. Applications: LE0516 is intended for strippable outer semi conductive shielding of XLPE medium voltage cables with rated voltages up to 36 kV. Specifications: AEIC CS8-00 (1st edition); BS 6622; ICEA S-94-649; IEC 60502; NF C33-223; NF C33-226; and UTE C 33-223.Information provided by Borealis AG

Physical Properties	Metric	English	Comments
Density	1.13 g/cc	0.0408 lb/in³	ISO 1183/ISO 1872-2
Water Absorption	0.080 %	0.080 %	Karl Fischer-titration

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	15.0 MPa	2180 psi	ISO 527
Elongation at Break	400 %	400 %	25mm/min; ISO 527

Electrical Properties	Metric	English	Comments
Volume Resistivity	<= 100 ohm-cm @Temperature 23.0 °C	<= 100 ohm-cm @Temperature 73.4 °F	ISO 3915
	<= 1000 ohm-cm @Temperature 90.0 °C	<= 1000 ohm-cm @Temperature 194 °F	ISO 3915

Processing Properties	Metric	English	Comments
Processing Temperature	40.0 °C	104 °F	drying temperature; under agitation with a dewpoint of -35°C
	280 °C	536 °F	maximum surface temperature, curing tube
Feed Temperature	>= 40.0 °C	>= 104 °F
Melt Temperature	120 - 140 °C	248 - 284 °F
Shelf Life	12.0 Month	12.0 Month

Descriptive Properties	Value	Comments
Göttfert Elastograph (Nm)	0.6-1.0
Hot Set Test, %	0	200°C, 0.2 MPa; IEC 60811-2-1; Permanent Deformation
	25	200°C, 0.2 MPa;IEC 60811-2-1; Elongation under load