Borealis LE0511 Polyethylene Compound, Crosslinkable, Semiconductive

Category Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer Borealis
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis LE0511 Polyethylene Compound, Crosslinkable, Semiconductive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LE0511 is a crosslinkable black polyethylene compound, specially designed for strippable semi conductive screen applications. Applications: LE0511 is intended for strippable outer semi conductive shielding of XLPE medium voltage cables with rated voltages up to 36 kV. Specifications: AEIC CS8-00 (1st edition); BS 6622; ICEA S-94-649; ICEA S-97-682; IEC 60502; NF C33-223; NF C33-226; and UTE C 33-22.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 1.17 g/cc
0.0423 lb/in³
ASTM D792
Water Absorption 0.15 %
0.15 %
Karl Fischer-titration
Mechanical Properties Metric English Comments
Tensile Strength at Break 15.0 MPa
2180 psi
25mm/min; ISO 527
Elongation at Break 300 %
300 %
25mm/min; ASTM D527
Electrical Properties Metric English Comments
Volume Resistivity 100 ohm-cm

@Temperature 23.0 °C
100 ohm-cm

@Temperature 73.4 °F
ISO 3915
1000 ohm-cm

@Temperature 90.0 °C
1000 ohm-cm

@Temperature 194 °F
ISO 3915
Processing Properties Metric English Comments
Processing Temperature 40.0 °C
104 °F
drying temperature; under agitation with a dewpoint of -35°C
280 °C
536 °F
maximum surface temperature, curing tube
Feed Temperature >= 40.0 °C
>= 104 °F
Melt Temperature 115 - 125 °C
239 - 257 °F
Shelf Life 18.0 Month
18.0 Month
Descriptive Properties Value Comments
Hot Set Test, % 0
200°C, 0.2 MPa; IEC 60811-2-1; Permanent Deformation
25
200°C, 0.2 MPa;IEC 60811-2-1; Elongation under load
Monsanto ODR (dNm) 26-34