- HOME
- POLYMER SEARCH
- Thermoplastic
- Polyethylene (PE)
- LDPE
- Low Density Polyethylene (LDPE), Film Grade
- Borealis Himod™ FT3280 LDPE for Film
Borealis Himod™ FT3280 LDPE for Film
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | Borealis |
| Trade Name | Himod™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Borealis Himod™ FT3280 LDPE for Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Himod FT3280 is a tubular, low-density polyethylene grade for the production of packaging films. Compared to standard LDPE grades, the Himod products provide a combination of higher stiffness and improved optical properties. Benefits can be obtained in terms of better down gauging possibilities and improved processability. Excellent printing quality is obtained due to high clarity and better layout.Himod FT3280 is intended for applications like: Stiff, transparent shrink films with high surface gloss and co-extrusion applications.Information provided by the Manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.928 g/cc | 0.0335 lb/in³ | ISO 1183 |
| Thickness | 40.0 microns | 1.57 mil | |
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.30 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 300 % | 300 % | ISO 527-3 |
| Film Elongation at Break, TD | 550 % | 550 % | ISO 527-3 |
| Secant Modulus, MD | 0.290 GPa | 42.1 ksi | ASTM D882-A |
| Secant Modulus, TD | 0.300 GPa | 43.5 ksi | ASTM D882-A |
| Impact | 71.4 | 71.4 | Puncture Resistance, force (N); ASTM D5748 |
| Puncture Energy | 3.20 J | 2.36 ft-lb | ASTM D5748 |
| Coefficient of Friction, Dynamic | 0.50 | 0.50 | ISO 8295 |
| Tear Strength, Total | 2.10 N | 0.472 lb (f) | TD; ISO 6383/2 |
| 2.40 N | 0.540 lb (f) | MD; ISO 6383/2 | |
| Dart Drop | 2.50 g/micron | 63.5 g/mil | ISO 7765/1 |
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | >= 117 °C | >= 243 °F | ISO 11357/03 |
| Vicat Softening Point | 106 °C | 223 °F | A (10N); ISO 306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 6.0 % | 6.0 % | ASTM D1003 |
| Gloss | 100 % | 100 % | ASTM D2457 |
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |