Borealis FG5223 Linear Low Density Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer Borealis
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis FG5223 Linear Low Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FG5223 is a Butene Linear Low Density Polyethylene for Film Extrusion. Includes antioxidant and anti-block additives. This grade is developed for production of lamination film. FG5223 has good heat sealing properties and hot tack strength. By mixing with FG5224 any desired level of friction can be obtained. Applications: lamination films, high clarity shrink film, and food wrap film.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 0.922 g/cc
0.0333 lb/in³
ISO 1183
Melt Flow 0.90 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.90 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Antiblock Level 1250 ppm
1250 ppm
Borealis Method
Mechanical Properties Metric English Comments
Tensile Strength, Yield 12.0 MPa
1740 psi
MD/TD; ISO 527-3
Film Elongation at Break, MD 800 %
800 %
ISO 527-3
Film Elongation at Break, TD 1000 %
1000 %
ISO 527-3
Tensile Modulus 0.145 GPa
21.0 ksi
MD; ASTM D882-A
0.165 GPa
23.9 ksi
TD; ASTM D882-A
Coefficient of Friction 0.70
0.70
Dynamic; ISO 8295
Elmendorf Tear Strength, MD 2.91 g/micron
73.9 g/mil
ISO 6383/2
Elmendorf Tear Strength, TD 13.11 g/micron
333.0 g/mil
ISO 6383/2
Dart Drop Test 260 g

@Thickness 0.0700 mm
0.573 lb

@Thickness 0.00276 in
ISO 7765-1
Film Tensile Strength at Break, MD 29.0 MPa
4210 psi
ISO 527-3
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 122 °C
252 °F
ISO 11357-3
Optical Properties Metric English Comments
Haze 10 %
10 %
ASTM D1003
Gloss 100 %
100 %
ASTM D2457