Borealis FA6224 Low Density Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer Borealis
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis FA6224 Low Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FA6224 is a Low Density Polyethylene for Film Extrusion. Autoclave Technology. Contains Antioxidant, Anti-block and Medium Slip additives. This grade is developed for the production of thin blown films. Applications: pouches, and general packaging film.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 0.922 g/cc
0.0333 lb/in³
ISO 1183
Melt Flow 2.1 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.1 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Antiblock Level 850 ppm
850 ppm
talc; Borealis Method
Slip Level 500 ppm
500 ppm
erucamide; Borealis Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 350 %
350 %
ISO 527-3
Film Elongation at Break, TD 600 %
600 %
ISO 527-3
Tensile Modulus 0.200 GPa
29.0 ksi
MD; ASTM D882-A
0.210 GPa
30.5 ksi
TD; ASTM D882-A
Puncture Energy 1.30 J
0.959 ft-lb
50 N; 40µm sample; ASTM D5748
Coefficient of Friction 0.10
0.10
Dynamic; ISO 8295
Elmendorf Tear Strength, MD 12.7 g/micron
323 g/mil
ISO 6383/2
Elmendorf Tear Strength, TD 7.65 g/micron
194 g/mil
ISO 6383/2
Dart Drop Test 100 g

@Thickness 0.0400 mm
0.221 lb

@Thickness 0.00157 in
ISO 7765-1
Film Tensile Strength at Break, MD 26.0 MPa
3770 psi
ISO 527-3
Film Tensile Strength at Break, TD 20.0 MPa
2900 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 111 °C
232 °F
ISO 11357-3
Vicat Softening Point 95.0 °C
203 °F
ISO 306
Optical Properties Metric English Comments
Haze 7.0 %
7.0 %
ASTM D1003
Gloss 85 %
85 %
ASTM D2457
Processing Properties Metric English Comments
Melt Temperature 150 - 180 °C
302 - 356 °F